CaTiOSiO4 - CaTiOGeO4 join Ellemann-Olesen R, Malcherek T American Mineralogist 90 (2005) 1325-1334 A high-temperature diffraction study of the solid solution CaTiOSiO4 - CaTiOGeO4 Note: Titanite structure Sample: #70, CaTiO(Ge.68Si.32)O4 _database_code_amcsd 0003884 CELL PARAMETERS: 7.1182 8.8322 6.6178 90.000 113.767 90.000 SPACE GROUP: P2_1/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 380.765 Density (g/cm3): 3.945 MAX. ABS. INTENSITY / VOLUME**2: 19.64967547 RIR: 1.622 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.76 4.25 4.9949 0 1 1 4 18.44 12.48 4.8104 -1 1 1 4 24.35 7.08 3.6554 1 2 0 4 25.83 13.55 3.4488 1 1 1 4 27.27 100.00 3.2708 -2 1 1 4 27.38 11.42 3.2572 2 0 0 2 29.50 85.59 3.0283 0 0 2 2 31.19 16.88 2.8679 -2 0 2 2 33.85 79.04 2.6478 0 3 1 4 33.90 6.97 2.6442 -1 2 2 4 34.21 55.98 2.6213 2 2 0 4 35.96 3.90 2.4975 0 2 2 4 37.39 7.41 2.4052 -2 2 2 4 37.65 6.58 2.3891 2 1 1 4 38.91 18.44 2.3148 1 3 1 4 39.36 2.26 2.2889 -3 1 1 4 39.92 12.41 2.2586 -2 3 1 4 40.87 2.06 2.2080 0 4 0 2 42.44 1.95 2.1298 -1 1 3 4 43.27 1.61 2.0912 1 4 0 4 43.38 17.67 2.0858 -2 1 3 4 45.33 4.36 2.0007 -3 2 2 4 46.12 2.76 1.9681 0 1 3 4 47.94 6.42 1.8975 2 3 1 4 48.61 6.81 1.8731 2 0 2 2 49.90 9.27 1.8277 2 4 0 4 51.94 15.30 1.7605 -4 0 2 2 51.97 1.02 1.7595 -1 3 3 4 52.29 9.31 1.7496 -2 4 2 4 52.78 6.16 1.7345 -2 3 3 4 53.03 1.43 1.7268 -4 1 1 4 53.11 19.53 1.7244 2 2 2 4 55.16 28.31 1.6650 0 3 3 4 56.50 6.55 1.6286 4 0 0 2 58.45 17.64 1.5789 -2 5 1 4 59.73 2.51 1.5482 3 4 0 4 59.81 8.85 1.5462 -2 2 4 4 61.21 6.07 1.5141 0 0 4 2 61.35 19.29 1.5111 -4 3 1 4 61.94 1.27 1.4981 1 3 3 4 63.16 3.14 1.4720 0 6 0 2 64.19 4.61 1.4509 2 1 3 4 64.78 8.47 1.4391 2 5 1 4 65.04 11.80 1.4339 -4 0 4 2 65.33 1.89 1.4284 2 4 2 4 65.51 7.52 1.4248 -4 3 3 4 68.83 9.54 1.3640 -2 5 3 4 69.98 1.35 1.3444 -1 6 2 4 70.89 1.50 1.3294 0 5 3 4 71.23 6.57 1.3239 0 6 2 4 71.34 2.28 1.3221 -2 4 4 4 72.13 1.18 1.3095 -1 4 4 4 73.43 8.29 1.2895 4 3 1 4 76.37 1.28 1.2470 -4 5 1 4 76.82 4.26 1.2408 4 0 2 2 77.56 1.45 1.2309 -3 6 2 4 79.42 1.12 1.2066 -2 3 5 4 79.91 1.58 1.2005 2 0 4 2 80.51 1.20 1.1931 -3 3 5 4 83.44 1.92 1.1585 2 2 4 4 84.82 3.33 1.1431 -4 3 5 4 86.00 2.02 1.1303 2 5 3 4 86.10 3.05 1.1293 -4 6 2 4 86.54 1.62 1.1247 2 7 1 4 86.98 4.18 1.1202 0 3 5 4 89.81 3.02 1.0921 4 6 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.