CaTiOSiO4 - CaTiOGeO4 join Ellemann-Olesen R, Malcherek T American Mineralogist 90 (2005) 1325-1334 A high-temperature diffraction study of the solid solution CaTiOSiO4 - CaTiOGeO4 Note: Titanite structure Sample: #50, CaTiO(Ge.49Si.51)O4 _database_code_amcsd 0003885 CELL PARAMETERS: 7.0953 8.7917 6.5962 90.000 113.757 90.000 SPACE GROUP: P2_1/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 376.606 Density (g/cm3): 3.842 MAX. ABS. INTENSITY / VOLUME**2: 18.91750876 RIR: 1.603 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.82 6.98 4.9768 0 1 1 4 18.51 5.98 4.7927 -1 1 1 4 24.45 4.74 3.6403 1 2 0 4 25.92 8.54 3.4373 1 1 1 4 27.36 100.00 3.2596 -2 1 1 4 27.47 8.42 3.2470 2 0 0 2 29.59 78.27 3.0186 0 0 2 2 31.29 12.73 2.8584 -2 0 2 2 32.95 1.14 2.7184 -2 1 2 4 34.01 74.21 2.6364 0 3 1 4 34.03 5.19 2.6343 -1 2 2 4 34.34 47.60 2.6118 2 2 0 4 36.09 2.17 2.4884 0 2 2 4 37.53 5.55 2.3964 -2 2 2 4 37.78 5.66 2.3815 2 1 1 4 39.07 16.92 2.3055 1 3 1 4 39.50 3.76 2.2814 -3 1 1 4 40.08 9.93 2.2495 -2 3 1 4 41.07 2.08 2.1979 0 4 0 2 42.59 3.33 2.1228 -1 1 3 4 43.47 3.10 2.0819 1 4 0 4 43.54 16.47 2.0788 -2 1 3 4 45.50 3.71 1.9936 -3 2 2 4 46.28 2.91 1.9617 0 1 3 4 48.13 4.70 1.8904 2 3 1 4 48.77 5.67 1.8673 2 0 2 2 50.12 8.89 1.8201 2 4 0 4 52.12 14.47 1.7549 -4 0 2 2 52.52 9.80 1.7424 -2 4 2 4 52.99 4.58 1.7280 -2 3 3 4 53.22 1.94 1.7212 -4 1 1 4 53.30 17.78 1.7187 2 2 2 4 55.38 26.29 1.6589 0 3 3 4 56.70 5.44 1.6235 4 0 0 2 58.73 15.24 1.5721 -2 5 1 4 59.98 1.83 1.5423 3 4 0 4 60.04 7.92 1.5409 -2 2 4 4 61.43 5.16 1.5093 0 0 4 2 61.59 17.32 1.5057 -4 3 1 4 63.49 2.62 1.4653 0 6 0 2 64.42 4.02 1.4464 2 1 3 4 65.08 7.35 1.4332 2 5 1 4 65.29 10.84 1.4292 -4 0 4 2 65.60 2.06 1.4231 2 4 2 4 65.78 6.40 1.4197 -4 3 3 4 69.15 8.45 1.3584 -2 5 3 4 70.33 1.15 1.3386 -1 6 2 4 71.21 1.05 1.3241 0 5 3 4 71.58 5.95 1.3182 0 6 2 4 71.65 2.14 1.3171 -2 4 4 4 73.72 7.69 1.2852 4 3 1 4 77.10 3.61 1.2370 4 0 2 2 77.95 1.07 1.2257 -3 6 2 4 80.21 1.21 1.1967 2 0 4 2 83.77 1.69 1.1547 2 2 4 4 85.19 2.83 1.1391 -4 3 5 4 86.40 1.47 1.1261 2 5 3 4 86.54 1.31 1.1247 -4 -6 2 4 87.00 1.76 1.1199 2 7 1 4 87.35 3.76 1.1164 0 3 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.