CaTiOSiO4 - CaTiOGeO4 join Ellemann-Olesen R, Malcherek T American Mineralogist 90 (2005) 1325-1334 A high-temperature diffraction study of the solid solution CaTiOSiO4 - CaTiOGeO4 Note: Titanite structure Sample: #20, CaTiO(Ge.20Si.80)O4 _database_code_amcsd 0003887 CELL PARAMETERS: 7.0718 8.7437 6.5730 90.000 113.782 90.000 SPACE GROUP: P2_1/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 371.925 Density (g/cm3): 3.659 MAX. ABS. INTENSITY / VOLUME**2: 16.82499657 RIR: 1.497 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.90 15.46 4.9556 0 1 1 4 18.59 3.39 4.7739 -1 1 1 4 24.57 1.23 3.6226 1 2 0 4 26.03 4.32 3.4235 1 1 1 4 27.46 100.00 3.2479 -2 1 1 4 27.57 7.58 3.2357 2 0 0 2 29.43 1.05 3.0345 2 1 0 4 29.71 77.20 3.0074 0 0 2 2 31.40 9.32 2.8491 -2 0 2 2 33.07 5.26 2.7089 -2 1 2 4 34.18 1.64 2.6232 -1 2 2 4 34.19 70.16 2.6229 0 3 1 4 34.48 49.85 2.6008 2 2 0 4 36.25 1.20 2.4778 0 2 2 4 37.69 4.30 2.3869 -2 2 2 4 37.93 4.35 2.3724 2 1 1 4 39.27 18.54 2.2944 1 3 1 4 39.64 5.66 2.2735 -3 1 1 4 40.28 5.20 2.2392 -2 3 1 4 41.30 2.58 2.1859 0 4 0 2 42.75 5.87 2.1150 -1 1 3 4 43.22 2.21 2.0933 1 2 2 4 43.70 14.95 2.0715 -2 1 3 4 43.71 6.48 2.0710 1 4 0 4 45.68 3.55 1.9863 -3 2 2 4 46.47 5.05 1.9542 0 1 3 4 48.36 2.53 1.8821 2 3 1 4 48.96 4.26 1.8603 2 0 2 2 50.38 8.95 1.8113 2 4 0 4 52.30 11.03 1.7491 -4 0 2 2 52.42 1.11 1.7455 -1 3 3 4 52.79 10.88 1.7343 -2 4 2 4 53.23 4.16 1.7209 -2 3 3 4 53.42 2.66 1.7152 -4 1 1 4 53.53 17.91 1.7118 2 2 2 4 55.64 24.05 1.6519 0 3 3 4 56.92 4.05 1.6178 4 0 0 2 56.93 1.28 1.6176 -4 0 3 2 59.06 11.89 1.5642 -2 5 1 4 60.14 1.13 1.5386 3 3 1 4 60.28 1.25 1.5354 3 4 0 4 60.29 5.85 1.5352 -2 2 4 4 61.68 5.20 1.5037 0 0 4 2 61.86 17.46 1.4998 -4 3 1 4 62.48 1.08 1.4866 1 3 3 4 63.88 2.30 1.4573 0 6 0 2 64.69 4.40 1.4409 2 1 3 4 65.44 6.52 1.4262 2 5 1 4 65.53 8.98 1.4245 -4 0 4 2 65.93 1.81 1.4167 2 4 2 4 66.06 7.20 1.4143 -4 3 3 4 69.52 8.38 1.3521 -2 5 3 4 72.00 2.60 1.3116 -2 4 4 4 72.01 6.23 1.3114 0 6 2 4 72.79 1.06 1.2992 -2 1 5 4 74.06 6.72 1.2801 4 3 1 4 77.44 4.05 1.2324 4 0 2 2 78.39 1.43 1.2198 -3 6 2 4 80.57 1.16 1.1922 2 0 4 2 84.17 1.54 1.1502 2 2 4 4 85.57 2.59 1.1349 -4 3 5 4 86.89 1.32 1.1211 2 5 3 4 87.03 1.12 1.1196 -4 -6 2 4 87.56 2.51 1.1142 2 7 1 4 87.78 3.77 1.1120 0 3 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.