Dissakisite-(La) Lavina B, Carbonin S, Russo U, Tumiati S American Mineralogist 91 (2006) 104-110 The crystal structure of dissakisite-(La) and structural variations after annealing of radiation damage Sample: DISS3 annealed 700 C for 3 hours _database_code_amcsd 0003996 8.931 5.699 10.182 90 115.16 90 P2_1/m atom x y z occ Uiso U(1,1) U(2,2) U(3,3) U(1,2) U(1,3) U(2,3) CaA1 .75676 .75 .15098 .792 .01441 .0219 .01197 .01385 0 .01192 0 ThA1 .75676 .75 .15098 .090 .01441 .0219 .01197 .01385 0 .01192 0 FeA1 .75676 .75 .15098 .053 .01441 .0219 .01197 .01385 0 .01192 0 LaA1 .75676 .75 .15098 .050 .01441 .0219 .01197 .01385 0 .01192 0 MnA1 .75676 .75 .15098 .009 .01441 .0219 .01197 .01385 0 .01192 0 UA1 .75676 .75 .15098 .003 .01441 .0219 .01197 .01385 0 .01192 0 NaA1 .75676 .75 .15098 .002 .01441 .0219 .01197 .01385 0 .01192 0 ErA1 .75676 .75 .15098 .001 .01441 .0219 .01197 .01385 0 .01192 0 CaA2 .59815 .75 .42772 .403 .01512 .01314 .01802 .01193 0 .00314 0 LaA2 .59815 .75 .42772 .265 .01512 .01314 .01802 .01193 0 .00314 0 CeA2 .59815 .75 .42772 .262 .01512 .01314 .01802 .01193 0 .00314 0 NdA2 .59815 .75 .42772 .038 .01512 .01314 .01802 .01193 0 .00314 0 PrA2 .59815 .75 .42772 .019 .01512 .01314 .01802 .01193 0 .00314 0 SrA2 .59815 .75 .42772 .010 .01512 .01314 .01802 .01193 0 .00314 0 SmA2 .59815 .75 .42772 .002 .01512 .01314 .01802 .01193 0 .00314 0 GdA2 .59815 .75 .42772 .001 .01512 .01314 .01802 .01193 0 .00314 0 AlM1 0 0 0 .813 .00884 .00864 .00667 .00919 -.00025 .00185 -.0001 CrM1 0 0 0 .148 .00884 .00864 .00667 .00919 -.00025 .00185 -.0001 TiM1 0 0 0 .030 .00884 .00864 .00667 .00919 -.00025 .00185 -.0001 VM1 0 0 0 .008 .00884 .00864 .00667 .00919 -.00025 .00185 -.0001 ScM1 0 0 0 .002 .00884 .00864 .00667 .00919 -.00025 .00185 -.0001 GaM1 0 0 0 .001 .00884 .00864 .00667 .00919 -.00025 .00185 -.0001 AlM2 0 0 .5 .948 .00755 .00718 .00583 .00855 .00023 .00228 -.00049 FeM2 0 0 .5 .052 .00755 .00718 .00583 .00855 .00023 .00228 -.00049 MgM3 .29705 .25 .21835 .622 .01147 .00976 .00772 .01071 0 -.00164 0 FeM3 .29705 .25 .21835 .299 .01147 .00976 .00772 .01071 0 -.00164 0 AlM3 .29705 .25 .21835 .054 .01147 .00976 .00772 .01071 0 -.00164 0 ZnM3 .29705 .25 .21835 .015 .01147 .00976 .00772 .01071 0 -.00164 0 NiM3 .29705 .25 .21835 .010 .01147 .00976 .00772 .01071 0 -.00164 0 Si1 .33785 .75 .04123 .990 .00789 .00779 .00657 .00817 0 .00227 0 Al1 .33785 .75 .04123 .007 .00789 .00779 .00657 .00817 0 .00227 0 P1 .33785 .75 .04123 .003 .00789 .00779 .00657 .00817 0 .00227 0 Si2 .68312 .25 .27672 .990 .00891 .01004 .0074 .00968 0 .00459 0 Al2 .68312 .25 .27672 .007 .00891 .01004 .0074 .00968 0 .00459 0 P2 .68312 .25 .27672 .003 .00891 .01004 .0074 .00968 0 .00459 0 Si3 .1859 .75 .32015 .990 .00693 .0067 .00799 .00644 0 .00312 0 Al3 .1859 .75 .32015 .007 .00693 .0067 .00799 .00644 0 .00312 0 P3 .1859 .75 .32015 .003 .00693 .0067 .00799 .00644 0 .00312 0 O1 .23395 .99227 .03345 .01446 .01058 .00993 .02286 .00204 .0071 .00269 O2 .30815 .9775 .35892 .01408 .01486 .01609 .01226 -.00611 .00671 -.00397 O3 .7928 .01355 .33786 .01681 .01576 .00879 .01748 .00062 -.00103 -.00169 O4 .05441 .25 .12967 .01137 .01087 .01073 .01136 0 .00362 0 O5 .04534 .75 .14737 .0097 .00826 .0112 .00781 0 .00165 0 O6 .06627 .75 .40663 .01269 .01582 .01211 .0152 0 .01147 0 O7 .51268 .75 .17843 .01612 .01234 .01625 .01292 0 -.00124 0 O8 .5318 .25 .3199 .02888 .02711 .03586 .03543 0 .02461 0 O9 .61971 .25 .10057 .0265 .03222 .03909 .01193 0 .01299 0 O10 .08335 .25 .42807 .01243 .01196 .01146 .01549 0 .00741 0 H .154 .25 .305 .05