Co3Al2Si3O12 Taran M N, Nestola F, Ohashi H, Koch-Muller M, Balic-Zunic T, Olsen L A American Mineralogist 92 (2007) 1616-1623 High-pressure optical spectroscopy and X-ray diffraction studies on synthetic cobalt aluminum silicate garnet Locality: Synthetic Sample: P = 0.0001 GPa _database_code_amcsd 0004454 CELL PARAMETERS: 11.4586 11.4586 11.4586 90.000 90.000 90.000 SPACE GROUP: Ia-3d X-RAY WAVELENGTH: 1.541838 Cell Volume: 1504.509 Density (g/cm3): 4.476 MAX. ABS. INTENSITY / VOLUME**2: 42.58629343 RIR: 3.098 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.97 9.95 4.6780 2 1 1 24 21.94 4.04 4.0512 2 2 0 12 29.16 6.02 3.0624 3 2 1 48 31.22 29.71 2.8647 4 0 0 6 35.02 100.00 2.5622 4 2 0 24 36.79 1.90 2.4430 3 3 2 24 38.49 21.63 2.3390 4 2 2 24 40.13 8.26 2.2472 4 3 1 48 43.25 16.71 2.0920 5 2 1 48 44.74 3.71 2.0256 4 4 0 12 49.01 10.42 1.8588 5 3 2 48 49.01 10.04 1.8588 6 1 1 24 55.57 14.93 1.6539 4 4 4 8 58.05 29.75 1.5890 6 4 0 24 59.26 1.73 1.5593 5 5 2 24 60.46 32.96 1.5312 6 4 2 48 63.98 1.08 1.4552 6 5 1 48 65.13 9.31 1.4323 8 0 0 6 73.99 7.01 1.2811 8 4 0 24 76.14 15.42 1.2502 8 4 2 48 78.27 5.16 1.2215 6 6 4 24 86.65 1.34 1.1236 10 2 0 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.