Co3Al2Si3O12 Taran M N, Nestola F, Ohashi H, Koch-Muller M, Balic-Zunic T, Olsen L A American Mineralogist 92 (2007) 1616-1623 High-pressure optical spectroscopy and X-ray diffraction studies on synthetic cobalt aluminum silicate garnet Locality: Synthetic Sample: P = 2.99 GPa _database_code_amcsd 0004457 CELL PARAMETERS: 11.3956 11.3956 11.3956 90.000 90.000 90.000 SPACE GROUP: Ia-3d X-RAY WAVELENGTH: 1.541838 Cell Volume: 1479.829 Density (g/cm3): 4.551 MAX. ABS. INTENSITY / VOLUME**2: 43.23148455 RIR: 3.093 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.08 10.77 4.6522 2 1 1 24 22.06 3.97 4.0290 2 2 0 12 29.33 6.30 3.0456 3 2 1 48 31.40 29.56 2.8489 4 0 0 6 35.22 100.00 2.5481 4 2 0 24 37.00 1.93 2.4296 3 3 2 24 38.71 22.21 2.3261 4 2 2 24 40.36 8.15 2.2349 4 3 1 48 43.50 17.16 2.0805 5 2 1 48 45.00 3.75 2.0145 4 4 0 12 49.29 10.14 1.8486 6 1 1 24 49.29 10.46 1.8486 5 3 2 48 55.90 14.92 1.6448 4 4 4 8 58.40 30.70 1.5803 6 4 0 24 59.62 1.12 1.5507 7 2 1 48 59.62 1.83 1.5507 5 5 2 24 60.83 33.49 1.5228 6 4 2 48 64.37 1.15 1.4472 6 5 1 48 65.53 9.58 1.4245 8 0 0 6 74.47 7.19 1.2741 8 4 0 24 76.64 15.65 1.2434 8 4 2 48 78.78 5.30 1.2148 6 6 4 24 87.24 1.32 1.1174 10 2 0 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.