Gismondine Ori S, Quartieri S, Vezzalini G, Dmitriev V American Mineralogist 93 (2008) 1393-1403 Pressure-induced over-hydration and water ordering in gismondine: a synchrotron powder diffraction study Locality: Ballyclare, Ireland Note: pressure = 0 after decompression _database_code_amcsd 0004634 10.0264 10.6094 9.8377 90 92.369 90 P2_1/c atom x y z occ Uiso Ca .7164 .0793 .356 .071 All .094 .112 .166 .025 Al2 .593 .866 .148 .025 Sil .412 .108 .181 .025 Si2 .909 .869 .160 .025 O1 .077 .168 .999 .013 O2 .261 .062 .212 .013 O3 .435 .157 .027 .013 O4 .243 .406 .303 .013 O5 .006 .982 .215 .013 O6 .048 .244 .254 .013 O7 .459 .231 .269 .013 O8 .505 .988 .222 .013 Watl .248 .110 .502 .035 Wat2 .585 .117 .552 .035 Wat3 .911 .120 .492 .035 Wat4 .802 .268 .246 .44 .035 Wat5 .749 .294 .392 .56 .035 Wat6 .754 .11 .01 .16 .035 Wat7 .750 .194 .168 .79 .035