NaVSi2O6 Ullrich A, Miletich R, Nestola F, Weikusat C, Ohashi H American Mineralogist 94 (2009) 557-564 Lattice compression and structural behavior of NaVSi2O6 clinopyroxene to 11 GPa Note: P = 0.0001 GPa _database_code_amcsd 0004897 CELL PARAMETERS: 9.6440 8.7490 5.3040 90.000 106.960 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 428.063 Density (g/cm3): 3.508 MAX. ABS. INTENSITY / VOLUME**2: 15.40771459 RIR: 1.430 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.95 31.39 6.3479 1 1 0 4 19.24 1.27 4.6123 2 0 0 2 20.09 15.66 4.4193 -1 1 1 4 20.30 20.41 4.3745 0 2 0 2 24.56 7.35 3.6242 1 1 1 4 26.91 1.35 3.3130 0 2 1 4 28.11 4.80 3.1740 2 2 0 4 30.06 100.00 2.9724 -2 2 1 4 30.82 46.67 2.9009 3 1 0 4 31.02 8.57 2.8833 -3 1 1 4 35.37 1.34 2.5376 -1 1 2 4 35.39 41.20 2.5367 0 0 2 2 35.42 22.41 2.5342 -1 3 1 4 36.27 38.10 2.4765 2 2 1 4 39.81 4.47 2.2641 3 1 1 4 40.87 17.68 2.2078 1 1 2 4 41.13 2.33 2.1944 0 2 2 4 42.73 3.18 2.1160 3 3 0 4 42.88 17.70 2.1091 -3 3 1 4 43.32 9.73 2.0884 -4 2 1 4 44.74 9.22 2.0256 -4 0 2 2 45.14 8.06 2.0085 0 4 1 4 45.56 5.36 1.9909 2 0 2 2 46.28 1.22 1.9619 -1 3 2 4 47.22 6.66 1.9247 -2 4 1 4 48.46 2.96 1.8785 -5 1 1 4 49.59 2.26 1.8381 -4 2 2 4 49.92 2.61 1.8270 3 3 1 4 50.56 1.81 1.8052 5 1 0 4 50.81 1.21 1.7970 1 3 2 4 51.69 2.01 1.7683 2 4 1 4 52.49 2.38 1.7434 4 2 1 4 53.29 9.88 1.7191 1 5 0 4 54.19 3.59 1.6926 3 1 2 4 54.80 1.61 1.6753 -3 1 3 4 55.47 6.62 1.6565 0 4 2 4 56.27 16.07 1.6349 -2 2 3 4 57.39 15.28 1.6056 -5 3 1 4 58.13 7.09 1.5870 4 4 0 4 59.00 1.03 1.5655 5 1 1 4 60.19 3.98 1.5374 6 0 0 2 60.65 4.48 1.5270 -6 0 2 2 60.92 5.13 1.5208 3 5 0 4 61.46 2.24 1.5086 -6 2 1 4 61.63 10.65 1.5048 -1 3 3 4 61.76 4.48 1.5022 4 0 2 2 63.11 1.66 1.4731 -3 3 3 4 63.78 1.53 1.4594 -5 1 3 4 63.83 4.94 1.4582 0 6 0 2 65.72 2.53 1.4207 4 2 2 4 67.00 15.27 1.3968 5 3 1 4 67.03 9.35 1.3962 -3 5 2 4 67.45 1.84 1.3885 1 5 2 4 67.82 4.57 1.3818 2 2 3 4 68.35 3.37 1.3724 -2 4 3 4 71.17 7.64 1.3248 -7 1 2 4 71.48 3.51 1.3198 -5 3 3 4 72.54 2.05 1.3031 7 1 0 4 72.55 2.81 1.3030 6 2 1 4 72.68 4.83 1.3009 -3 1 4 4 74.06 1.84 1.2802 -4 0 4 2 74.86 3.54 1.2683 0 0 4 2 74.95 1.45 1.2671 -2 6 2 4 75.15 7.78 1.2642 0 6 2 4 77.01 1.10 1.2383 4 4 2 4 77.73 6.81 1.2285 3 5 2 4 78.83 1.59 1.2142 -1 7 1 4 80.55 2.13 1.1925 1 7 1 4 83.32 1.27 1.1597 -8 2 1 4 83.46 3.05 1.1582 -6 0 4 2 83.91 1.08 1.1531 8 0 0 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.