NaVSi2O6 Ullrich A, Miletich R, Nestola F, Weikusat C, Ohashi H American Mineralogist 94 (2009) 557-564 Lattice compression and structural behavior of NaVSi2O6 clinopyroxene to 11 GPa Note: P = 3.47 GPa _database_code_amcsd 0004899 CELL PARAMETERS: 9.5660 8.6590 5.2520 90.000 106.820 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 416.422 Density (g/cm3): 3.606 MAX. ABS. INTENSITY / VOLUME**2: 15.29028249 RIR: 1.381 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.08 31.42 6.2914 1 1 0 4 19.39 1.71 4.5784 2 0 0 2 20.30 15.10 4.3744 -1 1 1 4 20.51 20.21 4.3295 0 2 0 2 24.77 7.34 3.5944 1 1 1 4 27.18 1.39 3.2806 0 2 1 4 28.37 3.99 3.1457 2 2 0 4 30.37 100.00 2.9427 -2 2 1 4 31.07 49.02 2.8786 3 1 0 4 31.31 8.84 2.8568 -3 1 1 4 35.72 41.41 2.5137 0 0 2 2 35.73 1.73 2.5127 -1 1 2 4 35.80 24.26 2.5082 -1 3 1 4 36.59 40.70 2.4561 2 2 1 4 40.12 4.79 2.2476 3 1 1 4 41.24 17.17 2.1891 1 1 2 4 41.54 2.02 2.1738 0 2 2 4 43.14 3.64 2.0971 3 3 0 4 43.32 17.84 2.0887 -3 3 1 4 43.74 10.87 2.0697 -4 2 1 4 45.20 9.82 2.0060 -4 0 2 2 45.63 7.97 1.9883 0 4 1 4 45.94 6.11 1.9754 2 0 2 2 46.77 1.76 1.9423 -1 3 2 4 47.74 5.95 1.9051 -2 4 1 4 48.90 3.30 1.8627 -5 1 1 4 50.12 2.26 1.8201 -4 2 2 4 50.37 2.08 1.8117 3 3 1 4 50.97 1.91 1.7917 5 1 0 4 51.31 1.08 1.7807 1 3 2 4 52.21 2.32 1.7519 2 4 1 4 52.92 2.41 1.7302 4 2 1 4 53.88 9.80 1.7016 1 5 0 4 54.64 3.75 1.6798 3 1 2 4 55.40 1.48 1.6583 -3 1 3 4 56.07 7.39 1.6403 0 4 2 4 56.12 1.17 1.6388 -1 5 1 4 56.89 17.05 1.6185 -2 2 3 4 57.95 14.93 1.5913 -5 3 1 4 58.70 6.95 1.5729 4 4 0 4 59.47 1.11 1.5543 5 1 1 4 60.68 4.02 1.5261 6 0 0 2 61.26 4.75 1.5131 -6 0 2 2 61.57 5.53 1.5062 3 5 0 4 62.04 2.42 1.4960 -6 2 1 4 62.24 1.07 1.4917 -4 2 3 4 62.26 4.58 1.4913 4 0 2 2 62.31 10.74 1.4901 -1 3 3 4 63.84 1.47 1.4581 -3 3 3 4 64.49 1.79 1.4448 -5 1 3 4 64.58 4.98 1.4432 0 6 0 2 66.29 2.53 1.4100 4 2 2 4 67.59 16.06 1.3859 5 3 1 4 67.81 9.09 1.3820 -3 5 2 4 68.19 1.89 1.3752 1 5 2 4 68.47 4.56 1.3703 2 2 3 4 69.14 3.67 1.3586 -2 4 3 4 71.91 7.77 1.3131 -7 1 2 4 72.31 3.54 1.3066 -5 3 3 4 73.17 2.77 1.2935 6 2 1 4 73.17 1.97 1.2934 7 1 0 4 73.54 4.73 1.2879 -3 1 4 4 74.94 1.87 1.2672 -4 0 4 2 75.67 3.44 1.2568 0 0 4 2 75.86 1.51 1.2541 -2 6 2 4 76.04 7.36 1.2516 0 6 2 4 77.77 1.17 1.2281 4 4 2 4 78.56 7.07 1.2176 3 5 2 4 79.81 1.44 1.2017 -1 7 1 4 81.54 2.23 1.1805 1 7 1 4 84.16 1.30 1.1504 -8 2 1 4 84.50 3.04 1.1466 -6 0 4 2 84.68 1.04 1.1446 8 0 0 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.