NaVSi2O6 Ullrich A, Miletich R, Nestola F, Weikusat C, Ohashi H American Mineralogist 94 (2009) 557-564 Lattice compression and structural behavior of NaVSi2O6 clinopyroxene to 11 GPa Note: P = 9.39 GPa _database_code_amcsd 0004901 CELL PARAMETERS: 9.4690 8.5210 5.1690 90.000 105.990 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 400.926 Density (g/cm3): 3.745 MAX. ABS. INTENSITY / VOLUME**2: 15.20739940 RIR: 1.322 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.24 32.39 6.2207 1 1 0 4 19.50 1.99 4.5513 2 0 0 2 20.67 13.77 4.2969 -1 1 1 4 20.85 20.50 4.2605 0 2 0 2 24.95 7.33 3.5686 1 1 1 4 27.58 1.37 3.2344 0 2 1 4 28.70 2.88 3.1104 2 2 0 4 30.91 100.00 2.8927 -2 2 1 4 31.29 50.31 2.8584 3 1 0 4 31.81 9.08 2.8133 -3 1 1 4 36.10 1.25 2.4879 -2 0 2 2 36.15 41.73 2.4845 0 0 2 2 36.32 2.33 2.4732 -1 1 2 4 36.42 27.59 2.4667 -1 3 1 4 36.87 46.43 2.4381 2 2 1 4 40.28 5.07 2.2392 3 1 1 4 41.60 17.50 2.1708 1 1 2 4 42.10 1.53 2.1462 0 2 2 4 42.43 1.43 2.1302 0 4 0 2 43.65 4.21 2.0736 3 3 0 4 44.04 18.99 2.0561 -3 3 1 4 44.38 11.52 2.0414 -4 2 1 4 46.07 11.65 1.9701 -4 0 2 2 46.20 7.44 1.9649 2 0 2 2 46.38 7.60 1.9579 0 4 1 4 47.57 2.74 1.9116 -1 3 2 4 48.59 5.56 1.8739 -2 4 1 4 49.52 3.68 1.8409 -5 1 1 4 50.80 1.88 1.7972 3 3 1 4 51.08 2.34 1.7881 -4 2 2 4 51.32 1.79 1.7803 5 1 0 4 51.92 1.00 1.7612 1 3 2 4 52.87 2.89 1.7316 2 4 1 4 53.21 2.49 1.7215 4 2 1 4 54.80 9.47 1.6751 1 5 0 4 54.89 3.91 1.6725 3 1 2 4 56.53 1.33 1.6281 -3 1 3 4 56.94 8.46 1.6172 0 4 2 4 57.13 1.69 1.6123 -1 5 1 4 57.94 18.35 1.5915 -2 2 3 4 58.78 14.16 1.5708 -5 3 1 4 59.43 7.09 1.5552 4 4 0 4 59.70 1.25 1.5488 5 1 1 4 61.08 4.30 1.5171 6 0 0 2 62.31 5.31 1.4902 -6 0 2 2 62.48 5.03 1.4865 4 0 2 2 62.51 6.20 1.4859 3 5 0 4 62.82 2.75 1.4793 -6 2 1 4 63.35 11.43 1.4681 -1 3 3 4 63.55 1.10 1.4641 -4 2 3 4 65.13 1.11 1.4323 -3 3 3 4 65.75 5.21 1.4202 0 6 0 2 65.86 2.13 1.4181 -5 1 3 4 66.63 2.64 1.4035 4 2 2 4 68.07 17.99 1.3774 5 3 1 4 69.08 4.84 1.3596 2 2 3 4 69.15 8.97 1.3585 -3 5 2 4 69.21 2.03 1.3574 1 5 2 4 70.47 4.28 1.3362 -2 4 3 4 73.09 8.28 1.2946 -7 1 2 4 73.56 2.95 1.2876 6 2 1 4 73.70 2.16 1.2855 7 1 0 4 73.86 3.56 1.2830 -5 3 3 4 75.05 4.78 1.2657 -3 1 4 4 76.59 2.04 1.2440 -4 0 4 2 76.72 3.40 1.2423 0 0 4 2 77.37 1.49 1.2334 -2 6 2 4 77.40 6.99 1.2330 0 6 2 4 78.45 1.30 1.2190 4 4 2 4 79.50 7.43 1.2056 3 5 2 4 81.38 1.30 1.1824 -1 7 1 4 83.06 2.44 1.1628 1 7 1 4 85.18 1.36 1.1392 -8 2 1 4 85.30 1.22 1.1378 8 0 0 2 86.51 2.87 1.1250 -6 0 4 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.