NaVSi2O6 Ullrich A, Miletich R, Nestola F, Weikusat C, Ohashi H American Mineralogist 94 (2009) 557-564 Lattice compression and structural behavior of NaVSi2O6 clinopyroxene to 11 GPa Note: P = 6.10 GPa _database_code_amcsd 0004905 CELL PARAMETERS: 9.5190 8.5980 5.2080 90.000 106.310 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 409.092 Density (g/cm3): 3.670 MAX. ABS. INTENSITY / VOLUME**2: 15.36770166 RIR: 1.363 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.15 31.11 6.2612 1 1 0 4 19.43 2.04 4.5680 2 0 0 2 20.49 14.41 4.3342 -1 1 1 4 20.66 20.72 4.2990 0 2 0 2 24.84 7.68 3.5844 1 1 1 4 27.36 1.52 3.2593 0 2 1 4 28.51 3.48 3.1306 2 2 0 4 30.64 100.00 2.9178 -2 2 1 4 31.16 49.45 2.8706 3 1 0 4 31.57 9.01 2.8343 -3 1 1 4 35.79 1.03 2.5092 -2 0 2 2 35.93 41.41 2.4992 0 0 2 2 36.04 2.14 2.4921 -1 1 2 4 36.09 25.60 2.4887 -1 3 1 4 36.69 42.99 2.4496 2 2 1 4 40.15 4.84 2.2457 3 1 1 4 41.40 17.18 2.1811 1 1 2 4 41.81 1.81 2.1606 0 2 2 4 43.35 3.54 2.0871 3 3 0 4 43.66 18.80 2.0730 -3 3 1 4 44.05 10.99 2.0557 -4 2 1 4 45.67 10.72 1.9865 -4 0 2 2 45.96 7.68 1.9747 0 4 1 4 46.03 6.80 1.9717 2 0 2 2 47.16 2.12 1.9273 -1 3 2 4 48.13 5.80 1.8906 -2 4 1 4 49.20 3.36 1.8519 -5 1 1 4 50.53 2.02 1.8063 3 3 1 4 50.62 2.44 1.8033 -4 2 2 4 51.11 1.75 1.7873 5 1 0 4 51.57 1.15 1.7721 1 3 2 4 52.49 2.57 1.7435 2 4 1 4 53.00 2.51 1.7277 4 2 1 4 54.28 9.88 1.6899 1 5 0 4 54.71 3.92 1.6778 3 1 2 4 56.00 1.46 1.6420 -3 1 3 4 56.47 7.69 1.6297 0 4 2 4 56.58 1.34 1.6267 -1 5 1 4 57.43 17.72 1.6044 -2 2 3 4 58.35 14.85 1.5815 -5 3 1 4 59.01 7.36 1.5653 4 4 0 4 59.52 1.12 1.5531 5 1 1 4 60.84 4.04 1.5227 6 0 0 2 61.81 5.11 1.5010 -6 0 2 2 61.97 5.73 1.4974 3 5 0 4 62.30 4.81 1.4904 4 0 2 2 62.41 2.53 1.4880 -6 2 1 4 62.82 11.25 1.4792 -1 3 3 4 62.93 1.05 1.4769 -4 2 3 4 64.50 1.35 1.4447 -3 3 3 4 65.09 5.28 1.4330 0 6 0 2 65.23 1.96 1.4303 -5 1 3 4 66.39 2.65 1.4082 4 2 2 4 67.75 17.35 1.3830 5 3 1 4 68.45 8.97 1.3706 -3 5 2 4 68.64 2.02 1.3674 1 5 2 4 68.73 4.67 1.3658 2 2 3 4 69.80 3.98 1.3474 -2 4 3 4 72.51 8.17 1.3035 -7 1 2 4 73.12 3.53 1.2942 -5 3 3 4 73.28 2.86 1.2918 6 2 1 4 73.37 2.08 1.2904 7 1 0 4 74.34 4.78 1.2760 -3 1 4 4 75.83 1.94 1.2546 -4 0 4 2 76.18 3.44 1.2496 0 0 4 2 76.56 1.53 1.2444 -2 6 2 4 76.65 7.49 1.2431 0 6 2 4 78.02 1.24 1.2248 4 4 2 4 78.94 7.28 1.2128 3 5 2 4 80.51 1.41 1.1931 -1 7 1 4 82.20 2.47 1.1727 1 7 1 4 84.63 1.33 1.1452 -8 2 1 4 84.92 1.21 1.1420 8 0 0 2 85.58 2.96 1.1348 -6 0 4 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.