Ulvospinel Yamanaka T, Kyono A, Nakamoto Y, Meng Y, Kharlamova S, Struzhkin V V, Mao H American Mineralogist 98 (2013) 736-744 High-pressure phase transitions of Fe3-xTixO4 solid solution up to 60 GPa correlated with electronic spin transition Locality: synthetic Note: P = 50 GPa _database_code_amcsd 0019932 CELL PARAMETERS: 2.6850 9.2280 9.0990 90.000 90.000 90.000 SPACE GROUP: Cmcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 225.448 Density (g/cm3): 6.585 MAX. ABS. INTENSITY / VOLUME**2: 55.41741568 RIR: 2.740 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.24 1.06 4.6140 0 2 0 2 19.51 1.74 4.5495 0 0 2 2 21.59 1.16 4.1152 0 2 1 4 34.80 1.67 2.5781 1 1 0 4 35.42 100.00 2.5345 0 2 3 4 36.21 27.84 2.4804 1 1 1 8 39.04 26.59 2.3070 0 4 0 2 39.62 3.34 2.2747 0 0 4 2 40.21 27.53 2.2430 1 1 2 8 40.33 4.69 2.2362 0 4 1 4 44.40 10.07 2.0403 0 2 4 4 44.81 14.13 2.0228 1 3 0 4 45.96 55.08 1.9746 1 3 1 8 49.30 24.47 1.8483 1 3 2 8 53.74 8.24 1.7057 1 1 4 8 54.18 2.18 1.6929 0 2 5 4 56.84 3.92 1.6198 0 4 4 4 61.11 8.63 1.5165 0 0 6 2 61.85 6.50 1.5001 1 5 1 8 62.47 23.35 1.4867 1 1 5 8 63.89 4.50 1.4570 0 6 2 4 64.61 11.30 1.4425 1 5 2 8 68.39 7.34 1.3717 0 6 3 4 69.09 8.61 1.3596 1 5 3 8 69.48 10.11 1.3529 1 3 5 8 70.09 10.85 1.3425 2 0 0 2 74.94 9.38 1.2672 0 4 6 4 75.14 1.86 1.2644 1 5 4 8 76.07 1.19 1.2512 0 2 7 4 78.89 1.07 1.2134 1 3 6 8 81.06 12.45 1.1863 2 2 3 8 81.31 3.02 1.1833 1 7 0 4 82.14 2.99 1.1735 1 7 1 8 82.69 2.79 1.1670 1 5 5 8 83.27 4.43 1.1603 2 4 0 4 83.88 3.52 1.1535 0 8 0 2 86.85 1.35 1.1215 2 2 4 8 89.66 2.26 1.0935 1 3 7 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.