Tuite Thompson R M, Xie X, Zhai S, Downs R T, Yang H American Mineralogist 98 (2013) 1585-1592 A comparison of the Ca3(PO4)2 and CaSiO3 systems, with a new structure refinement of tuite synthesized at 15 GPa and 1300 deg C Locality: synthetic _database_code_amcsd 0020245 CELL PARAMETERS: 5.2522 5.2522 18.6900 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 446.501 Density (g/cm3): 3.460 MAX. ABS. INTENSITY / VOLUME**2: 22.11556129 RIR: 2.081 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 20.09 1.74 4.4195 1 0 1 6 28.66 4.28 3.1150 0 0 6 2 30.97 85.76 2.8879 0 1 5 6 34.14 100.00 2.6261 1 1 0 6 37.15 4.43 2.4199 1 1 3 12 40.84 22.59 2.2098 2 0 2 6 43.55 5.49 2.0782 0 1 8 6 43.58 9.38 2.0767 0 0 9 2 44.30 14.10 2.0449 0 2 4 6 45.16 6.78 2.0078 1 1 6 12 46.75 44.97 1.9429 2 0 5 6 52.88 2.54 1.7313 0 2 7 6 52.97 25.71 1.7287 1 0 10 6 56.49 2.17 1.6289 1 1 9 12 59.15 18.85 1.5619 1 2 5 12 61.12 14.00 1.5162 3 0 0 6 64.54 6.71 1.4440 0 2 10 6 67.66 1.17 1.3847 1 2 8 12 68.99 3.25 1.3612 2 0 11 6 71.91 18.83 1.3131 2 2 0 6 75.07 16.56 1.2653 2 1 10 12 80.33 8.38 1.1953 3 1 5 12 86.44 11.71 1.1257 1 1 15 12 88.00 2.97 1.1098 2 2 9 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.