Plattnerite Grocholski B, Shim S H, Cottrell E, Prakapenka V B American Mineralogist 99 (2014) 170-177 Crystal structure and compressibility of lead dioxide up to 140 GPa Note: P = 75.1 GPa Locality: Synthetic _database_code_amcsd 0020165 CELL PARAMETERS: 5.2980 6.2390 3.2690 90.000 90.000 90.000 SPACE GROUP: Pnam X-RAY WAVELENGTH: 1.541838 Cell Volume: 108.054 Density (g/cm3): 14.702 MAX. ABS. INTENSITY / VOLUME**2: 478.3667988 RIR: 10.595 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 28.62 2.90 3.1195 0 2 0 2 30.88 49.32 2.8956 0 1 1 4 33.33 91.07 2.6881 1 2 0 4 33.84 46.80 2.6490 2 0 0 2 35.32 100.00 2.5409 1 1 1 8 44.00 1.71 2.0581 2 0 1 4 44.89 2.79 2.0192 2 2 0 4 46.46 39.95 1.9545 2 1 1 8 52.12 26.58 1.7547 0 3 1 4 55.14 10.62 1.6657 1 3 1 8 56.28 14.03 1.6345 0 0 2 2 59.24 8.62 1.5597 0 4 0 2 60.22 18.47 1.5368 3 2 0 4 61.50 19.28 1.5077 3 1 1 8 62.03 2.06 1.4963 1 4 0 4 63.61 21.99 1.4629 2 3 1 8 67.01 20.08 1.3966 1 2 2 8 67.31 10.50 1.3910 2 0 2 4 70.00 8.36 1.3441 2 4 0 4 71.19 4.42 1.3245 4 0 0 2 76.54 2.68 1.2447 3 3 1 8 79.59 4.19 1.2045 4 1 1 8 85.24 8.70 1.1385 1 5 1 8 86.19 4.76 1.1284 0 4 2 4 87.03 10.48 1.1196 3 2 2 8 88.62 1.29 1.1037 1 4 2 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.