Clinozoisite Nagashima M, Geiger C A, Akasaka M American Mineralogist 94 (2009) 1351-1360 A crystal-chemical investigation of clinozoisite synthesized along the join Ca2Al3Si3O12(OH)-Ca2Al2CrSi3O12(OH) Locality: synthetic Note: T = 700 C, P = 1.2 GPa _database_code_amcsd 0004979 CELL PARAMETERS: 8.8889 5.6058 10.1513 90.000 115.284 90.000 SPACE GROUP: P2_1/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 457.375 Density (g/cm3): 3.404 MAX. ABS. INTENSITY / VOLUME**2: 8.760902853 RIR: 0.838 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.64 3.21 9.1788 0 0 1 2 11.01 11.02 8.0374 1 0 0 2 11.11 2.18 7.9630 -1 0 1 2 17.69 29.23 5.0126 -1 0 2 2 18.55 2.49 4.7841 0 1 1 4 19.36 2.51 4.5839 -1 1 1 4 22.12 14.56 4.0187 2 0 0 2 22.33 15.55 3.9815 -2 0 2 2 23.67 5.54 3.7596 1 1 1 4 23.81 1.12 3.7366 -1 1 2 4 25.58 28.87 3.4825 -2 1 1 4 26.15 12.22 3.4077 1 0 2 2 27.78 12.19 3.2117 2 0 1 2 29.19 4.33 3.0596 0 0 3 2 30.51 2.43 2.9304 -3 0 1 2 30.62 16.16 2.9195 -3 0 2 2 30.90 100.00 2.8941 -1 1 3 4 31.93 33.74 2.8029 0 2 0 2 32.12 12.89 2.7867 2 1 1 4 32.42 2.17 2.7619 -2 1 3 4 33.36 26.35 2.6856 0 1 3 4 33.45 18.60 2.6791 3 0 0 2 33.87 19.71 2.6466 1 2 0 4 33.91 1.37 2.6439 -1 2 1 4 34.54 37.71 2.5970 -3 1 1 4 34.64 1.00 2.5894 -3 1 2 4 35.42 15.76 2.5342 2 0 2 2 35.81 5.43 2.5073 -1 0 4 2 36.74 14.78 2.4464 -1 2 2 4 37.49 25.34 2.3990 -3 1 3 4 37.60 24.68 2.3921 0 2 2 4 37.95 4.11 2.3708 -2 2 1 4 39.15 4.86 2.3011 1 1 3 4 39.30 1.07 2.2924 -3 0 4 2 39.31 15.75 2.2919 -2 2 2 4 39.37 1.45 2.2888 -1 1 4 4 39.38 2.47 2.2880 -2 1 4 4 41.71 15.06 2.1656 -4 0 1 2 41.87 4.50 2.1574 -1 2 3 4 41.95 2.61 2.1539 -4 0 3 2 42.57 1.92 2.1237 0 1 4 4 42.82 21.52 2.1118 2 2 1 4 43.05 14.36 2.1009 -2 2 3 4 43.80 15.30 2.0668 0 2 3 4 43.83 1.70 2.0657 -4 1 2 4 44.21 6.12 2.0489 2 0 3 2 44.74 2.54 2.0255 -3 2 1 4 44.83 1.77 2.0219 -3 2 2 4 45.12 7.56 2.0093 4 0 0 2 45.51 1.13 1.9932 1 0 4 2 45.76 1.92 1.9829 -1 0 5 2 46.52 1.98 1.9523 -3 0 5 2 47.23 2.32 1.9244 2 1 3 4 48.42 7.05 1.8798 2 2 2 4 48.47 4.41 1.8780 1 1 4 4 48.71 3.41 1.8694 -1 1 5 4 48.73 6.72 1.8687 -1 2 4 4 48.74 13.81 1.8683 -2 2 4 4 48.89 3.60 1.8631 3 1 2 4 51.47 3.00 1.7756 0 2 4 4 51.60 4.64 1.7714 -5 0 2 2 52.45 1.80 1.7446 0 1 5 4 52.56 2.04 1.7413 -4 2 2 4 53.17 3.40 1.7225 -2 3 1 4 53.80 1.79 1.7038 2 0 4 2 53.82 5.44 1.7034 -4 1 5 4 54.29 2.65 1.6897 -2 0 6 2 54.31 2.82 1.6891 -5 1 2 4 54.43 1.39 1.6856 -5 1 3 4 54.95 1.97 1.6709 -3 0 6 2 56.16 12.05 1.6378 -5 1 1 4 56.20 10.41 1.6367 -1 0 6 2 56.26 10.80 1.6353 -1 3 3 4 56.34 3.38 1.6331 4 2 0 4 56.44 2.34 1.6302 2 1 4 4 56.67 7.20 1.6244 1 2 4 4 56.72 15.48 1.6230 -4 2 4 4 57.02 1.92 1.6151 2 3 1 4 57.04 4.12 1.6147 3 2 2 4 57.82 4.22 1.5947 0 3 3 4 58.13 12.76 1.5869 -4 0 6 2 58.52 5.93 1.5773 1 1 5 4 58.59 7.95 1.5755 -3 3 1 4 59.86 3.98 1.5452 5 1 0 4 59.92 5.18 1.5437 4 1 2 4 60.52 1.53 1.5298 0 0 6 2 60.60 3.97 1.5280 -3 3 3 4 61.52 1.75 1.5073 -4 2 5 4 61.97 1.37 1.4974 -5 2 2 4 63.67 1.91 1.4615 3 0 4 2 63.76 3.71 1.4597 -6 0 4 2 63.94 3.47 1.4559 2 2 4 4 64.01 10.21 1.4546 -5 2 4 4 64.38 4.75 1.4471 -2 2 6 4 64.39 1.05 1.4469 3 2 3 4 64.98 7.76 1.4352 -3 2 6 4 65.58 1.30 1.4236 4 0 3 2 66.53 3.31 1.4054 2 1 5 4 66.75 21.53 1.4015 0 4 0 2 67.13 2.32 1.3944 5 2 0 4 67.18 15.34 1.3934 4 2 2 4 67.87 1.18 1.3810 -4 2 6 4 68.88 1.79 1.3632 1 3 4 4 69.76 1.69 1.3481 5 0 2 2 70.07 2.50 1.3428 0 2 6 4 72.12 1.32 1.3097 -6 2 3 4 72.84 3.73 1.2985 -6 2 2 4 72.92 1.04 1.2973 -5 2 6 4 73.09 2.28 1.2947 -6 2 4 4 73.28 1.95 1.2918 -4 3 5 4 73.69 1.43 1.2856 -5 3 2 4 73.77 1.03 1.2845 2 4 1 4 74.02 1.54 1.2806 3 0 5 2 74.28 2.19 1.2768 0 1 7 4 74.80 4.46 1.2692 4 2 3 4 74.82 2.43 1.2689 -3 0 8 2 74.95 1.47 1.2671 4 0 4 2 75.21 1.90 1.2634 -3 4 2 4 75.24 1.39 1.2629 -6 2 1 4 75.27 5.42 1.2625 -5 3 1 4 75.73 5.30 1.2560 -6 2 5 4 75.90 1.53 1.2536 -2 0 8 2 76.12 1.25 1.2505 1 2 6 4 76.75 2.50 1.2418 3 4 0 4 77.31 2.50 1.2342 1 3 5 4 77.89 3.36 1.2264 2 4 2 4 78.49 1.76 1.2186 5 3 0 4 78.54 1.82 1.2179 4 3 2 4 79.25 3.23 1.2088 -6 1 7 4 80.94 2.46 1.1877 0 2 7 4 81.87 1.83 1.1766 -4 4 1 4 84.24 1.43 1.1495 4 4 0 4 84.51 1.57 1.1464 2 3 5 4 84.53 1.39 1.1462 -6 0 8 2 86.53 2.46 1.1248 7 1 0 4 87.50 1.82 1.1148 -7 1 7 4 87.85 1.66 1.1113 -1 2 8 4 87.92 1.78 1.1106 -5 2 8 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.