Fluoro-pargasite Oberti R, Sardone N, Hawthorne F C, Raudsepp M, Turnock A C The Canadian Mineralogist 33 (1995) 25-31 Synthesis and crystal-structure refinement of synthetic fluor-pargasite Sample FP2 [note: ideal = NaCa2(Mg4Al)(Si6Al2)O22(OH)2] Locality: Synthetic _database_code_amcsd 0005426 CELL PARAMETERS: 9.8080 17.8680 5.2970 90.000 105.300 90.000 SPACE GROUP: C2/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 895.395 Density (g/cm3): 3.901 MAX. ABS. INTENSITY / VOLUME**2: 36.45197147 RIR: 3.043 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.90 100.00 8.9340 0 2 0 2 17.36 20.41 5.1093 0 0 1 2 17.60 12.78 5.0403 1 3 0 4 18.11 6.19 4.8973 -1 1 1 4 18.76 15.39 4.7302 2 0 0 2 19.88 1.69 4.4670 0 4 0 2 20.02 20.99 4.4352 0 2 1 4 21.25 23.96 4.1804 2 2 0 4 21.98 12.77 4.0434 -2 0 1 2 24.16 17.21 3.6837 -2 2 1 4 26.50 7.20 3.3629 0 4 1 4 26.53 22.64 3.3598 1 3 1 4 26.67 8.30 3.3430 1 5 0 4 27.46 28.34 3.2477 2 4 0 4 28.75 6.35 3.1055 3 1 0 4 28.91 6.81 3.0885 2 0 1 2 29.80 7.25 2.9977 -2 4 1 4 30.63 32.00 2.9190 2 2 1 4 32.82 12.60 2.7287 -3 3 1 4 33.37 29.12 2.6851 1 5 1 4 34.87 17.20 2.5729 0 6 1 4 35.25 23.07 2.5462 -2 0 2 2 35.33 3.61 2.5404 2 4 1 4 35.62 1.50 2.5201 2 6 0 4 36.46 3.49 2.4644 1 7 0 4 36.58 6.29 2.4562 0 2 2 4 36.70 6.66 2.4487 -2 2 2 4 37.15 1.41 2.4200 -1 3 2 4 37.45 3.86 2.4014 -4 0 1 2 38.05 2.75 2.3651 4 0 0 2 38.06 7.33 2.3645 3 5 0 4 38.67 14.33 2.3286 -3 5 1 4 38.83 14.01 2.3191 -4 2 1 4 39.41 4.10 2.2863 4 2 0 4 39.42 1.38 2.2857 -3 1 2 4 39.49 11.90 2.2819 -1 7 1 4 40.32 2.04 2.2371 3 3 1 4 40.69 3.85 2.2176 0 4 2 4 40.79 7.11 2.2121 -2 4 2 4 41.77 1.00 2.1623 1 7 1 4 42.15 10.67 2.1437 2 6 1 4 42.48 4.92 2.1278 -1 5 2 4 42.75 2.17 2.1151 -4 4 1 4 43.29 2.48 2.0902 4 4 0 4 44.53 8.03 2.0345 2 0 2 2 44.83 7.40 2.0217 -4 0 2 2 45.34 7.17 2.0003 3 5 1 4 45.73 5.29 1.9840 3 7 0 4 45.74 3.45 1.9837 2 2 2 4 46.03 2.85 1.9719 -4 2 2 4 46.26 1.00 1.9627 -3 7 1 4 46.37 1.79 1.9583 4 0 1 2 46.72 1.21 1.9442 1 5 2 4 46.75 4.48 1.9430 1 9 0 4 46.91 3.33 1.9368 -3 5 2 4 46.95 1.02 1.9353 -2 6 2 4 47.53 1.18 1.9129 4 2 1 4 48.38 2.14 1.8816 5 1 0 4 48.71 1.58 1.8694 -4 6 1 4 49.26 6.25 1.8497 -1 9 1 4 49.49 4.00 1.8419 -4 4 2 4 49.60 4.56 1.8379 -1 7 2 4 50.62 1.82 1.8033 5 3 0 4 53.13 1.78 1.7239 -2 2 3 4 53.54 1.01 1.7116 -5 5 1 4 53.57 1.79 1.7106 -3 7 2 4 53.83 1.35 1.7031 0 0 3 2 54.38 2.37 1.6870 -1 3 3 4 54.63 2.15 1.6801 3 9 0 4 54.88 5.42 1.6730 0 2 3 4 54.91 1.33 1.6722 5 5 0 4 56.22 7.09 1.6362 4 6 1 4 57.57 4.66 1.6009 1 11 0 4 58.48 6.79 1.5782 -1 5 3 4 58.54 2.37 1.5767 6 0 0 2 58.77 1.02 1.5713 -4 2 3 4 59.54 1.86 1.5527 6 2 0 4 59.68 1.76 1.5495 -5 7 1 4 59.76 1.10 1.5475 -1 11 1 4 59.90 3.43 1.5442 4 0 2 2 60.30 4.69 1.5349 -6 0 2 2 60.88 1.78 1.5217 4 2 2 4 60.95 1.74 1.5200 5 7 0 4 61.25 6.81 1.5132 -2 6 3 4 61.51 2.91 1.5076 1 9 2 4 61.66 1.62 1.5042 -3 9 2 4 61.91 1.22 1.4989 -4 8 2 4 62.32 2.38 1.4898 5 5 1 4 62.36 1.29 1.4890 0 12 0 2 63.58 1.19 1.4633 1 5 3 4 63.77 1.76 1.4595 4 4 2 4 64.02 1.30 1.4544 3 7 2 4 64.53 2.82 1.4440 3 11 0 4 64.95 1.41 1.4358 -3 11 1 4 65.15 7.87 1.4318 -6 6 1 4 66.11 1.04 1.4135 -3 7 3 4 67.31 1.15 1.3911 -5 9 1 4 67.44 1.54 1.3886 6 2 1 4 68.91 2.19 1.3626 -5 5 3 4 69.37 1.51 1.3547 5 1 2 4 70.68 1.03 1.3327 -6 2 3 4 70.84 3.03 1.3301 1 11 2 4 70.99 1.99 1.3277 -3 11 2 4 71.02 1.83 1.3272 2 6 3 4 71.04 1.10 1.3270 -1 13 1 4 71.70 1.40 1.3164 -5 9 2 4 72.45 2.61 1.3045 -7 5 1 4 73.39 1.16 1.2902 -3 9 3 4 73.64 1.22 1.2864 0 12 2 4 73.71 1.14 1.2853 -2 12 2 4 74.25 1.21 1.2773 0 0 4 2 74.54 1.67 1.2731 -4 0 4 2 80.49 2.76 1.1932 -5 11 2 4 81.37 1.01 1.1825 8 0 0 2 83.42 1.71 1.1586 2 0 4 2 87.27 1.13 1.1172 7 9 0 4 87.41 1.17 1.1158 -6 4 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.