Haiweeite Burns P C The Canadian Mineralogist 39 (2001) 1153-1160 A new uranyl silicate sheet in the structure of haiweeite and comparison to other uranyl silicates _database_code_amcsd 0005732 CELL PARAMETERS: 7.1250 17.9370 18.3420 90.000 90.000 90.000 SPACE GROUP: Cmcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 2344.128 Density (g/cm3): 2.848 MAX. ABS. INTENSITY / VOLUME**2: 109.1694245 RIR: 12.483 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 9.64 100.00 9.1710 0 0 2 2 9.86 1.38 8.9685 0 2 0 2 10.98 21.84 8.0569 0 2 1 4 13.37 1.57 6.6217 1 1 0 4 13.81 5.39 6.4121 0 2 2 4 16.51 1.64 5.3686 1 1 2 8 17.56 13.02 5.0518 0 2 3 4 19.36 15.36 4.5855 0 0 4 2 19.76 2.03 4.4920 1 1 3 8 19.98 23.15 4.4436 1 3 1 8 20.39 1.52 4.3560 0 4 1 4 21.77 2.58 4.0828 0 2 4 4 23.60 3.45 3.7698 1 1 4 8 24.28 6.13 3.6656 1 3 3 8 25.00 14.24 3.5625 2 0 0 2 26.25 7.53 3.3953 0 2 5 4 26.85 13.17 3.3208 2 0 2 4 27.37 5.85 3.2582 2 2 1 8 27.84 9.85 3.2042 1 5 0 4 28.27 2.96 3.1564 1 5 1 8 28.67 1.32 3.1141 2 2 2 8 29.21 3.60 3.0570 0 0 6 2 29.53 16.49 3.0249 1 5 2 8 29.89 2.10 2.9895 0 6 0 2 30.71 4.14 2.9114 2 2 3 8 31.24 2.49 2.8632 1 3 5 8 31.52 1.82 2.8381 1 5 3 8 31.81 7.03 2.8133 2 0 4 4 34.14 9.47 2.6265 1 5 4 8 35.70 2.75 2.5151 0 2 7 4 36.56 2.29 2.4578 2 2 5 8 37.29 1.93 2.4112 1 7 0 4 37.62 2.77 2.3907 1 7 1 8 38.61 2.03 2.3320 1 7 2 8 38.82 2.59 2.3199 2 0 6 4 39.30 2.09 2.2927 0 0 8 2 39.63 1.99 2.2744 1 3 7 8 40.20 1.10 2.2431 1 7 3 8 40.53 2.39 2.2256 0 8 1 4 40.80 2.92 2.2118 1 5 6 8 41.19 5.03 2.1914 3 3 1 8 42.35 1.51 2.1342 1 7 4 8 42.97 1.68 2.1050 0 8 3 4 43.60 2.61 2.0761 3 3 3 8 44.07 1.74 2.0547 2 2 7 8 44.99 1.52 2.0149 1 7 5 8 45.65 1.61 1.9873 0 2 9 4 45.82 4.17 1.9803 3 5 0 4 46.94 4.39 1.9357 3 5 2 8 47.14 2.17 1.9280 2 0 8 4 47.53 1.47 1.9131 0 8 5 4 48.06 1.45 1.8932 1 7 6 8 48.11 2.21 1.8913 3 3 5 8 48.21 2.30 1.8875 2 8 1 8 48.84 3.46 1.8646 1 5 8 8 48.92 2.41 1.8620 1 3 9 8 49.71 1.84 1.8342 0 0 10 2 50.18 3.58 1.8180 3 5 4 8 50.35 1.38 1.8123 2 8 3 8 51.17 1.21 1.7852 0 10 1 4 51.29 1.18 1.7812 4 0 0 2 52.32 2.16 1.7486 4 0 2 4 52.62 1.39 1.7393 4 2 1 8 52.74 1.63 1.7356 2 2 9 8 54.35 1.04 1.6881 3 3 7 8 55.27 2.03 1.6621 3 5 6 8 55.29 1.14 1.6615 1 7 8 8 55.33 1.78 1.6604 4 0 4 4 56.42 1.30 1.6307 2 0 10 4 57.77 1.06 1.5960 2 10 1 8 57.93 1.48 1.5918 1 5 10 8 58.95 1.16 1.5668 1 3 11 8 61.91 1.92 1.4987 3 5 8 8 61.98 1.16 1.4973 3 3 9 8 67.95 1.29 1.3796 1 5 12 8 69.90 1.38 1.3457 3 5 10 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.