Spodumene Tribaudino M, Nestola F, Prencipe M, Rundlof H The Canadian Mineralogist 41 (2003) 521-527 A single-crystal neutron-diffraction investigation of spodumene at 54 K Sample: T = 298 K, X-ray radiation _database_code_amcsd 0005837 CELL PARAMETERS: 9.4790 8.4030 5.2230 90.000 110.140 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 390.585 Density (g/cm3): 3.164 MAX. ABS. INTENSITY / VOLUME**2: 10.53029902 RIR: 1.084 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.50 14.52 6.1098 1 1 0 4 19.95 11.03 4.4497 2 0 0 2 20.37 24.34 4.3604 -1 1 1 4 21.15 37.73 4.2015 0 2 0 2 25.85 23.66 3.4471 1 1 1 4 27.97 27.64 3.1905 0 2 1 4 29.23 2.60 3.0549 2 2 0 4 30.60 100.00 2.9213 -2 2 1 4 31.25 10.66 2.8624 -3 1 1 4 32.00 56.30 2.7973 3 1 0 4 33.54 6.96 2.6718 1 3 0 4 35.19 8.85 2.5504 -2 0 2 2 36.60 2.50 2.4552 -1 3 1 4 36.65 36.38 2.4518 0 0 2 2 38.22 13.40 2.3550 2 2 1 4 40.55 2.75 2.2248 4 0 0 2 41.42 1.71 2.1802 -2 2 2 4 42.06 5.90 2.1480 3 1 1 4 42.70 1.29 2.1176 0 2 2 4 42.87 17.41 2.1096 1 1 2 4 43.92 10.07 2.0613 -3 3 1 4 44.10 1.35 2.0535 -4 2 1 4 44.49 2.38 2.0366 3 3 0 4 44.59 2.80 2.0322 -4 0 2 2 47.06 9.98 1.9310 0 4 1 4 48.80 19.31 1.8662 -2 4 1 4 49.28 6.93 1.8490 -5 1 1 4 49.84 4.15 1.8295 -4 2 2 4 51.08 2.25 1.7881 -3 3 2 4 52.56 4.93 1.7412 5 1 0 4 53.14 1.41 1.7236 2 2 2 4 54.58 1.31 1.6814 -1 1 3 4 55.11 1.95 1.6665 -3 1 3 4 55.66 3.28 1.6514 1 5 0 4 56.78 2.68 1.6215 -2 4 2 4 57.30 15.85 1.6080 -2 2 3 4 57.46 8.44 1.6037 3 1 2 4 57.80 6.05 1.5953 0 4 2 4 58.83 21.72 1.5698 -5 3 1 4 60.62 7.08 1.5274 4 4 0 4 60.85 1.85 1.5223 -6 0 2 2 62.16 3.13 1.4933 1 1 3 4 62.31 1.71 1.4902 5 1 1 4 62.63 1.73 1.4832 6 0 0 2 63.59 7.84 1.4633 -1 3 3 4 63.61 2.44 1.4627 -5 1 3 4 63.64 3.48 1.4622 3 5 0 4 63.71 1.66 1.4606 -4 4 2 4 65.18 1.11 1.4312 -6 2 2 4 65.66 2.16 1.4219 4 0 2 2 66.80 6.47 1.4005 0 6 0 2 68.97 7.07 1.3616 -3 5 2 4 69.83 3.90 1.3469 4 2 2 4 69.85 1.05 1.3467 0 6 1 4 70.23 6.69 1.3403 -2 4 3 4 70.73 14.26 1.3320 5 3 1 4 71.63 3.17 1.3175 2 2 3 4 71.78 11.08 1.3150 -7 1 2 4 71.96 2.60 1.3123 -5 3 3 4 72.60 3.02 1.3023 -2 0 4 2 73.61 3.59 1.2869 -3 1 4 4 74.39 3.35 1.2752 -4 0 4 2 75.65 1.87 1.2570 7 1 0 4 76.68 1.40 1.2428 6 2 1 4 77.13 2.41 1.2366 5 1 2 4 77.80 3.68 1.2276 -2 6 2 4 77.93 2.10 1.2259 0 0 4 2 78.23 1.43 1.2220 5 5 0 4 78.68 9.44 1.2161 0 6 2 4 78.76 2.89 1.2151 -7 3 1 4 80.78 1.06 1.1897 1 7 0 4 82.31 6.37 1.1714 3 5 2 4 82.56 1.40 1.1685 -1 7 1 4 83.17 2.29 1.1615 -6 0 4 2 83.51 1.03 1.1577 7 3 0 4 84.28 1.13 1.1490 3 3 3 4 86.44 1.71 1.1258 -7 3 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.