Na2[(UO2)(MoO4)2](H2O)4 Krivovichev S V, Burns P C The Canadian Mineralogist 41 (2003) 707-719 Crystal chemistry of uranyl molybdates. VIII. Crystal structures of Na3Tl3[(UO2)(MoO4)4], Na13-xTl3+x[(UO2)(MoO4)3]4(H2O)6+x (x=0.1), Na3Tl5[(UO2)(MoO4)2]2(H2O)3 and Na2[(UO2)(MoO4)2](H2O)4 Sample 4 _database_code_amcsd 0005858 8.9023 11.5149 13.8151 90 107.743 90 P2_1/n atom x y z occ Uiso U(1,1) U(2,2) U(3,3) U(1,2) U(1,3) U(2,3) U .18365 .21151 .153504 .01401 .0162 .0128 .01238 -.0008 .00323 -.0005 Mo(1) .40090 .38523 .41116 .0162 .0205 .0131 .0123 -.0011 .0009 .0005 Mo(2) .35641 .51588 .12263 .0163 .0205 .0144 .0139 -.0021 .0051 -.0026 Na(1) .7878 .4105 .16643 .0285 .0315 .0254 .0302 .0008 .0119 .0009 Na(2) .2981 .4150 .6447 .0311 .0296 .0364 .0303 .0017 .0134 .0005 O(1) .5615 .2953 .4747 .0249 .040 .012 .020 .006 .006 -.0031 O(2) .4571 .5338 .3971 .0187 .027 .011 .018 .0000 .0061 -.0019 O(3) .0043 .2674 .1670 .0234 .026 .023 .020 .000 .005 .0020 O(4) .2536 .3824 .0842 .0253 .041 .024 .012 -.013 .009 -.0014 O(5) .3603 .1498 .1402 .0252 .021 .031 .026 -.002 .010 .003 O(6) .2665 .5994 .1991 .0207 .030 .019 .012 .002 .0046 -.0032 O(7) .5518 .4943 .1908 .0259 .020 .037 .021 -.001 .008 -.005 O(8) .2501 .3796 .4647 .0272 .026 .032 .022 -.007 .006 -.003 Wat(9) .0927 .5392 .6496 .0344 .034 .036 .031 .002 .008 -.003 O(10) .3489 .5953 .0147 .0276 .041 .022 .021 -.008 .010 .004 O(11) .3272 .3311 .2859 .0271 .037 .023 .015 -.007 -.002 .0004 O(12) .9297 .5649 .1316 .0372 .034 .041 .033 -.010 .004 .009 Wat(13) .1976 .2687 .7260 .0369 .034 .031 .051 .002 .021 -.003 Wat(14) .6078 .7461 .0680 .0446 .063 .050 .029 -.020 .026 -.010