Harmotome Stuckenschmidt E, Fuess H, Kvick A European Journal of Mineralogy 2 (1990) 861-874 Investigation of the structure of harmotome by X-ray (293 K, 100 K) and neutron diffraction (15 K) Sample: 293 K _database_code_amcsd 0006409 9.8688 14.1295 8.7092 90 124.74 90 P2_1/m atom x y z occ Biso U(1,1) U(2,2) U(3,3) U(1,2) U(1,3) U(2,3) Ba .8620 1/4 .1946 1.82 .0306 .0153 .0233 0 .0161 0 SiT1 .7363 .0235 .2848 .65 .75 .0079 .0119 .0086 .0012 .0039 -.0003 AlT1 .7363 .0235 .2848 .35 .75 .0079 .0119 .0086 .0012 .0039 -.0003 SiT2 .4211 .1410 .0148 .84 .70 .0077 .0075 .0113 .0009 .0049 -.0000 AlT2 .4211 .1410 .0148 .16 .70 .0077 .0075 .0113 .0009 .0049 -.0000 SiT3 .0578 .0086 .2901 .70 .84 .0095 .0132 .0091 .0000 .0061 .0009 AlT3 .0578 .0086 .2901 .30 .84 .0095 .0132 .0091 .0000 .0061 .0009 SiT4 .1187 .1391 .0341 .77 .92 .0126 .0095 .0129 -.0004 .0097 .0008 AlT4 .1187 .1391 .0341 .23 .92 .0126 .0095 .0129 -.0004 .0097 .0008 O1 .1002 .0928 .1927 2.80 .0373 .0413 .0278 -.0092 .0227 .0077 O2 .6485 .5746 .1674 1.67 .0240 .0197 .0196 .0054 .0107 .0064 O3 .6127 .1172 .1784 1.40 .0137 .0204 .0189 .0059 .0054 .0001 O4 .0060 .9083 .1738 1.89 .0244 .0263 .0211 -.0013 .0088 -.0090 O5 .9050 .0526 .2965 1.47 .0151 .0194 .0213 .0021 .0119 .0018 O6 .3111 .3692 .1001 2.04 .0187 .0330 .0257 -.0043 .0164 -.0043 O7 .7785 .4879 .4963 1.69 .0163 .0317 .0163 -.0036 .0099 -.0025 O8 .5845 3/4 .0524 1.91 .0347 .0111 .0268 0 .0207 0 O9 .0640 1/4 .0230 2.15 .0230 .0172 .0415 0 .0190 0 O10 .8041 3/4 .4924 4.50 .0605 .0747 .0356 0 .0167 0 O20 .1158 3/4 .4645 4.04 .0899 .0277 .0358 0 .0343 0 O30 .3010 .8627 .1271 4.69 .0613 .0749 .0420 -.0095 .0254 -.0225 O40 .512 1/4 .486 17.4 .211 .388 .0603 0 .0304 0 O50 .496 .562 .474 11.3 .0505 .314 .0656 .0459 .0334 .0850