Ulvospinel Sedler I K, Feenstra A, Peters T European Journal of Mineralogy 6 (1994) 873-885 An X-ray powder diffraction study of synthetic (Fe,Mn)2TiO4 spinel Sample: D-16 _database_code_amcsd 0006568 CELL PARAMETERS: 8.5439 8.5439 8.5439 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 623.689 Density (g/cm3): 4.761 MAX. ABS. INTENSITY / VOLUME**2: 68.90981075 RIR: 4.713 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.98 23.79 4.9328 1 1 1 8 29.57 23.32 3.0207 2 2 0 12 34.83 100.00 2.5761 3 1 1 24 36.43 10.62 2.4664 2 2 2 8 42.31 28.62 2.1360 4 0 0 6 46.32 1.34 1.9601 3 3 1 24 52.47 6.78 1.7440 4 2 2 24 55.92 27.67 1.6443 5 1 1 24 55.92 4.98 1.6443 3 3 3 8 61.38 41.47 1.5104 4 4 0 12 64.53 2.81 1.4442 5 3 1 48 69.59 2.21 1.3509 6 2 0 24 72.55 7.96 1.3029 5 3 3 24 73.53 4.88 1.2880 6 2 2 24 77.38 3.32 1.2332 4 4 4 8 80.24 1.15 1.1964 5 5 1 24 84.94 2.69 1.1417 6 4 2 48 87.75 5.16 1.1123 5 5 3 24 87.75 6.43 1.1123 7 3 1 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.