Ulvospinel Sedler I K, Feenstra A, Peters T European Journal of Mineralogy 6 (1994) 873-885 An X-ray powder diffraction study of synthetic (Fe,Mn)2TiO4 spinel Sample: D-10 _database_code_amcsd 0006575 CELL PARAMETERS: 8.6429 8.6429 8.6429 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 645.622 Density (g/cm3): 4.573 MAX. ABS. INTENSITY / VOLUME**2: 66.19707905 RIR: 4.713 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.77 21.35 4.9900 1 1 1 8 29.23 24.08 3.0557 2 2 0 12 34.41 100.00 2.6059 3 1 1 24 36.00 9.96 2.4950 2 2 2 8 41.81 28.10 2.1607 4 0 0 6 45.76 1.14 1.9828 3 3 1 24 51.82 7.48 1.7642 4 2 2 24 55.22 29.49 1.6633 5 1 1 24 55.22 5.33 1.6633 3 3 3 8 60.61 44.44 1.5279 4 4 0 12 63.70 2.79 1.4609 5 3 1 48 68.68 2.59 1.3666 6 2 0 24 71.59 9.03 1.3180 5 3 3 24 72.55 5.64 1.3030 6 2 2 24 76.34 3.54 1.2475 4 4 4 8 79.14 1.21 1.2102 5 5 1 24 83.75 3.28 1.1550 6 4 2 48 86.49 6.09 1.1252 5 5 3 24 86.49 7.82 1.1252 7 3 1 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.