CaU(PO4)2 Dusausoy Y, Ghermani N E, Podor R, Cuney M European Journal of Mineralogy 8 (1996) 667-673 Low-temperature ordered phase of CaU(PO4)2: synthesis and crystal structure _database_code_amcsd 0006629 CELL PARAMETERS: 13.9260 6.9580 6.1360 90.000 90.000 90.000 SPACE GROUP: Pnma X-RAY WAVELENGTH: 1.541838 Cell Volume: 594.561 Density (g/cm3): 5.228 MAX. ABS. INTENSITY / VOLUME**2: 68.06032260 RIR: 4.239 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.78 33.25 5.6151 1 0 1 4 18.02 100.00 4.9218 2 1 0 4 19.28 41.22 4.6036 2 0 1 4 19.29 41.84 4.6021 0 1 1 4 20.32 34.17 4.3697 1 1 1 8 24.04 15.04 3.7020 3 0 1 4 25.59 86.22 3.4815 4 0 0 2 25.61 87.25 3.4790 0 2 0 2 27.29 13.11 3.2682 3 1 1 8 29.82 16.24 2.9962 1 0 2 4 30.22 14.42 2.9574 1 2 1 8 32.24 24.05 2.7765 4 1 1 8 32.25 16.07 2.7756 2 2 1 8 32.54 66.31 2.7519 1 1 2 8 35.06 7.97 2.5595 3 0 2 4 35.39 2.96 2.5362 5 0 1 4 35.41 11.42 2.5352 3 2 1 8 36.51 33.40 2.4609 4 2 0 4 37.44 47.63 2.4021 3 1 2 8 37.75 6.36 2.3828 5 1 1 8 39.14 4.88 2.3018 4 0 2 4 39.15 2.38 2.3011 0 2 2 4 39.70 14.27 2.2703 1 2 2 8 40.99 13.14 2.2017 6 1 0 4 41.02 13.16 2.2005 2 3 0 4 41.60 17.41 2.1709 6 0 1 4 41.63 6.60 2.1695 0 3 1 4 42.15 16.97 2.1437 1 3 1 8 43.90 9.16 2.0622 5 0 2 4 43.92 8.08 2.0617 3 2 2 8 44.19 3.27 2.0494 5 2 1 8 44.79 3.20 2.0236 1 0 3 4 45.90 25.49 1.9772 5 1 2 8 46.19 9.54 1.9655 3 3 1 8 46.26 12.19 1.9624 2 0 3 4 46.27 4.38 1.9623 0 1 3 4 46.75 9.50 1.9431 1 1 3 8 48.08 3.21 1.8924 7 0 1 4 48.65 2.37 1.8717 3 0 3 4 49.49 16.15 1.8417 6 2 1 8 49.50 7.93 1.8413 4 3 1 8 49.71 24.87 1.8340 1 3 2 8 49.94 3.00 1.8261 7 1 1 8 50.49 4.04 1.8074 3 1 3 8 51.52 10.71 1.7740 5 2 2 8 52.30 3.74 1.7492 1 2 3 8 52.57 11.27 1.7407 8 0 0 2 52.61 11.95 1.7395 0 4 0 2 53.30 21.83 1.7187 3 3 2 8 53.54 7.72 1.7115 5 3 1 8 53.61 6.35 1.7095 4 1 3 8 53.62 7.94 1.7092 2 2 3 8 55.01 1.73 1.6692 7 0 2 4 55.26 4.26 1.6624 7 2 1 8 55.29 2.97 1.6616 1 4 1 8 55.77 2.93 1.6483 3 2 3 8 56.06 5.34 1.6406 6 3 0 4 56.52 5.40 1.6282 8 1 1 8 56.56 4.22 1.6272 2 4 1 8 56.71 17.83 1.6232 7 1 2 8 57.45 3.82 1.6042 5 1 3 8 58.64 3.01 1.5744 3 4 1 8 59.37 9.31 1.5568 8 2 0 4 59.40 9.66 1.5561 4 4 0 4 60.03 13.07 1.5411 5 3 2 8 60.32 2.31 1.5345 6 0 3 4 60.34 2.25 1.5340 0 3 3 4 60.34 3.78 1.5340 0 0 4 2 60.74 2.02 1.5248 1 3 3 8 61.63 2.35 1.5050 7 2 2 8 61.66 4.31 1.5043 1 4 2 8 62.33 1.22 1.4898 5 2 3 8 63.42 1.63 1.4667 9 1 1 8 63.44 2.87 1.4663 7 3 1 8 63.52 7.96 1.4645 2 1 4 8 64.80 2.79 1.4387 3 4 2 8 65.02 1.20 1.4345 5 4 1 8 65.45 1.23 1.4261 7 0 3 4 66.61 1.47 1.4040 6 2 3 8 66.62 3.64 1.4038 4 3 3 8 66.62 8.53 1.4038 4 0 4 4 66.63 7.70 1.4036 0 2 4 4 66.98 1.60 1.3971 7 1 3 8 67.84 2.78 1.3816 9 0 2 4 68.74 2.93 1.3655 10 1 0 4 68.80 2.92 1.3646 2 5 0 4 69.17 1.18 1.3581 10 0 1 4 69.19 3.09 1.3577 8 3 1 8 69.21 5.49 1.3575 6 4 1 8 69.23 1.45 1.3571 0 5 1 4 69.35 5.14 1.3551 9 1 2 8 69.36 11.80 1.3548 7 3 2 8 69.60 1.23 1.3507 1 5 1 8 70.87 4.27 1.3296 5 4 2 8 71.50 1.79 1.3195 7 2 3 8 71.52 1.42 1.3191 1 4 3 8 72.60 2.56 1.3022 8 1 3 8 72.63 16.60 1.3018 4 2 4 8 72.63 3.49 1.3017 2 4 3 8 73.80 4.16 1.2840 9 2 2 8 74.02 1.95 1.2807 7 4 1 8 74.46 1.26 1.2742 3 4 3 8 75.09 1.45 1.2651 10 2 1 8 75.13 2.29 1.2645 4 5 1 8 75.30 5.53 1.2621 1 5 2 8 75.46 2.63 1.2598 9 3 1 8 75.54 4.62 1.2586 6 1 4 8 75.56 5.33 1.2584 2 3 4 8 76.89 1.10 1.2399 11 0 1 4 77.59 4.77 1.2305 8 4 0 4 78.18 5.41 1.2226 3 5 2 8 78.76 1.58 1.2150 9 1 3 8 79.60 1.21 1.2044 7 4 2 8 80.44 1.92 1.1939 10 3 0 4 80.47 1.92 1.1935 6 5 0 4 81.01 3.81 1.1869 9 3 2 8 82.47 1.41 1.1696 3 1 5 8 82.61 1.83 1.1679 11 2 1 8 83.26 3.45 1.1605 12 0 0 2 83.33 3.84 1.1597 0 6 0 2 83.83 5.49 1.1541 11 1 2 8 83.87 4.09 1.1535 5 5 2 8 84.09 1.73 1.1511 10 0 3 4 84.11 1.91 1.1509 8 3 3 8 84.11 4.16 1.1509 8 0 4 4 84.12 1.06 1.1508 6 4 3 8 84.14 4.00 1.1505 0 4 4 4 84.49 1.60 1.1466 1 5 3 8 84.94 1.86 1.1417 4 1 5 8 84.95 2.91 1.1416 2 2 5 8 86.49 1.65 1.1253 12 1 1 8 86.56 1.70 1.1245 2 6 1 8 86.71 1.16 1.1229 3 2 5 8 86.95 3.62 1.1205 6 3 4 8 88.11 1.29 1.1087 5 1 5 8 88.70 1.05 1.1028 7 4 3 8 88.90 4.32 1.1009 12 2 0 4 88.96 4.66 1.1002 4 6 0 4 89.73 1.92 1.0928 10 2 3 8 89.75 8.93 1.0927 8 2 4 8 89.77 1.59 1.0924 4 5 3 8 89.77 9.38 1.0924 4 4 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.