Diopside-subsilisic Redhammer G J European Journal of Mineralogy 10 (1998) 439-452 Mossbauer spectroscopy and Rietveld refinement on synthetic ferri-Tschermak's molecule CaFe3+(Fe3+Si)O6 substituted diopside Sample: fts30/#2 _database_code_amcsd 0006724 CELL PARAMETERS: 9.7844 8.9132 5.2989 90.000 105.883 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 444.476 Density (g/cm3): 3.498 MAX. ABS. INTENSITY / VOLUME**2: 15.46209954 RIR: 1.439 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.92 4.40 4.4566 0 2 0 2 26.57 7.16 3.3549 0 2 1 4 27.57 18.64 3.2357 2 2 0 4 29.79 100.00 2.9990 -2 2 1 4 30.20 30.79 2.9590 3 1 0 4 30.78 27.01 2.9053 -3 1 1 4 34.94 28.72 2.5678 -1 3 1 4 35.16 1.39 2.5523 -2 0 2 2 35.22 39.16 2.5483 0 0 2 2 35.55 46.42 2.5251 2 2 1 4 38.26 1.29 2.3527 4 0 0 2 38.94 12.34 2.3128 3 1 1 4 40.41 9.87 2.2322 1 1 2 4 40.79 5.56 2.2122 0 2 2 4 41.88 6.78 2.1571 3 3 0 4 42.31 14.45 2.1360 -3 3 1 4 42.78 8.36 2.1135 -4 2 1 4 44.37 14.85 2.0417 0 4 1 4 44.71 11.73 2.0271 -4 0 2 2 44.84 5.82 2.0211 2 0 2 2 45.89 5.89 1.9774 -1 3 2 4 48.84 1.51 1.8646 3 3 1 4 49.50 5.17 1.8416 5 1 0 4 49.52 2.84 1.8407 2 2 2 4 50.08 2.45 1.8215 1 3 2 4 52.23 11.43 1.7515 1 5 0 4 52.98 1.33 1.7284 -5 1 2 4 53.14 1.04 1.7234 3 1 2 4 54.53 1.49 1.6830 -1 5 1 4 54.72 5.49 1.6774 0 4 2 4 54.94 5.21 1.6714 -3 1 3 4 56.22 16.27 1.6362 -2 2 3 4 56.50 13.93 1.6286 -5 3 1 4 56.92 5.45 1.6178 4 4 0 4 58.01 1.75 1.5900 5 3 0 4 58.88 3.31 1.5685 6 0 0 2 59.66 5.74 1.5499 3 5 0 4 60.23 5.13 1.5366 -6 0 2 2 60.42 7.10 1.5322 4 0 2 2 60.49 2.55 1.5306 -6 2 1 4 61.16 1.13 1.5154 -5 3 2 4 61.26 13.33 1.5130 -1 3 3 4 61.99 1.33 1.4970 2 4 2 4 62.52 4.57 1.4855 0 6 0 2 63.52 1.25 1.4646 4 4 1 4 64.10 1.78 1.4527 -6 2 2 4 64.29 1.47 1.4490 4 2 2 4 65.40 17.48 1.4269 5 3 1 4 65.44 1.88 1.4262 0 6 1 4 66.20 9.56 1.4116 -3 5 2 4 66.27 3.99 1.4103 1 5 2 4 66.84 5.18 1.3996 2 2 3 4 67.88 1.27 1.3807 -2 4 3 4 69.59 1.06 1.3510 0 4 3 4 70.47 6.38 1.3362 -7 1 2 4 70.74 4.09 1.3318 6 2 1 4 70.89 1.39 1.3294 7 1 0 4 71.25 3.54 1.3235 -5 3 3 4 72.85 4.32 1.2983 -3 1 4 4 72.92 1.55 1.2973 -1 1 4 4 73.80 2.78 1.2839 -2 6 2 4 73.84 5.09 1.2834 0 6 2 4 74.33 1.77 1.2761 -4 0 4 2 74.46 3.10 1.2742 0 0 4 2 75.11 1.17 1.2647 -7 3 1 4 75.27 1.34 1.2625 4 4 2 4 76.07 6.90 1.2512 3 5 2 4 77.22 1.46 1.2355 -1 7 1 4 78.81 2.30 1.2145 1 7 1 4 81.89 1.65 1.1764 8 0 0 2 83.67 3.19 1.1558 -6 0 4 2 87.38 1.39 1.1161 2 2 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.