Diopside-subsilisic Redhammer G J European Journal of Mineralogy 10 (1998) 439-452 Mossbauer spectroscopy and Rietveld refinement on synthetic ferri-Tschermak's molecule CaFe3+(Fe3+Si)O6 substituted diopside Sample: fts40/#1 _database_code_amcsd 0006725 CELL PARAMETERS: 9.8007 8.9002 5.3214 90.000 105.856 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 446.515 Density (g/cm3): 3.387 MAX. ABS. INTENSITY / VOLUME**2: 13.77708129 RIR: 1.324 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.68 3.30 6.4719 1 1 0 4 18.83 3.60 4.7139 2 0 0 2 19.95 3.61 4.4501 0 2 0 2 26.54 2.37 3.3584 0 2 1 4 27.56 16.86 3.2359 2 2 0 4 29.77 100.00 3.0013 -2 2 1 4 30.16 29.26 2.9633 3 1 0 4 30.72 24.76 2.9102 -3 1 1 4 34.95 29.80 2.5674 -1 3 1 4 35.06 42.82 2.5595 0 0 2 2 35.49 48.58 2.5294 2 2 1 4 38.18 1.22 2.3569 4 0 0 2 38.84 11.64 2.3186 3 1 1 4 40.25 11.97 2.2407 1 1 2 4 40.67 6.59 2.2187 0 2 2 4 41.88 7.95 2.1573 3 3 0 4 42.30 19.25 2.1365 -3 3 1 4 42.74 10.95 2.1158 -4 2 1 4 44.39 14.39 2.0406 0 4 1 4 44.58 12.14 2.0325 -4 0 2 2 44.67 8.17 2.0288 2 0 2 2 45.81 6.53 1.9808 -1 3 2 4 48.79 2.66 1.8666 3 3 1 4 49.37 2.48 1.8460 2 2 2 4 49.41 3.86 1.8446 5 1 0 4 49.97 2.30 1.8252 1 3 2 4 51.18 1.48 1.7847 4 2 1 4 52.30 12.81 1.7491 1 5 0 4 52.86 1.09 1.7321 -5 1 2 4 54.58 1.72 1.6815 -1 5 1 4 54.66 5.13 1.6792 0 4 2 4 54.72 5.19 1.6773 -3 1 3 4 56.01 16.99 1.6417 -2 2 3 4 56.46 14.04 1.6299 -5 3 1 4 56.91 5.35 1.6180 4 4 0 4 57.95 2.04 1.5913 5 3 0 4 58.76 3.72 1.5713 6 0 0 2 59.70 6.37 1.5488 3 5 0 4 60.09 5.91 1.5397 -6 0 2 2 60.20 6.99 1.5371 4 0 2 2 60.40 3.10 1.5326 -6 2 1 4 61.07 1.00 1.5174 -5 3 2 4 61.07 13.33 1.5173 -1 3 3 4 61.36 1.24 1.5108 -4 2 3 4 62.63 4.30 1.4834 0 6 0 2 63.98 1.62 1.4551 -6 2 2 4 64.09 1.27 1.4529 4 2 2 4 65.29 17.47 1.4291 5 3 1 4 65.52 2.04 1.4248 0 6 1 4 66.18 9.64 1.4120 -3 5 2 4 66.23 4.66 1.4112 1 5 2 4 66.58 5.01 1.4046 2 2 3 4 67.73 1.24 1.3834 -2 4 3 4 69.41 1.09 1.3540 0 4 3 4 70.32 6.04 1.3386 -7 1 2 4 70.58 4.33 1.3344 6 2 1 4 70.75 1.33 1.3317 7 1 0 4 71.08 3.63 1.3263 -5 3 3 4 72.52 3.69 1.3034 -3 1 4 4 72.56 1.55 1.3028 -1 1 4 4 73.82 2.28 1.2837 -2 6 2 4 73.84 4.65 1.2834 0 6 2 4 74.00 1.71 1.2809 -4 0 4 2 74.08 3.25 1.2797 0 0 4 2 75.12 1.27 1.2647 4 4 2 4 75.98 6.80 1.2525 3 5 2 4 77.32 1.63 1.2340 -1 7 1 4 78.90 2.37 1.2133 1 7 1 4 81.71 1.96 1.1785 8 0 0 2 83.35 3.37 1.1594 -6 0 4 2 86.96 1.31 1.1204 2 2 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.