Hedenbergite Redhammer G J, Amthauer G, Lottermoser W, Treutmann W European Journal of Mineralogy 12 (2000) 105-120 Synthesis and structural properties of clinopyroxenes of the hedenbergite CaFeSi2O6 - aegirine NaFeSi2O6 solid-solution series Sample: ae40/20 _database_code_amcsd 0006818 CELL PARAMETERS: 9.7598 8.9277 5.2748 90.000 106.041 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 441.712 Density (g/cm3): 3.627 MAX. ABS. INTENSITY / VOLUME**2: 19.34065326 RIR: 1.736 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.69 26.16 6.4668 1 1 0 4 18.92 6.40 4.6899 2 0 0 2 19.89 9.50 4.4639 0 2 0 2 20.09 5.61 4.4193 -1 1 1 4 24.29 2.72 3.6650 1 1 1 4 27.59 8.33 3.2334 2 2 0 4 29.81 100.00 2.9972 -2 2 1 4 30.29 40.17 2.9509 3 1 0 4 30.83 7.63 2.9002 -3 1 1 4 34.93 30.42 2.5686 -1 3 1 4 35.41 39.17 2.5347 0 0 2 2 35.49 2.10 2.5293 -1 1 2 4 35.67 43.03 2.5173 2 2 1 4 37.61 1.13 2.3917 1 3 1 4 38.39 2.12 2.3449 4 0 0 2 39.12 3.64 2.3025 3 1 1 4 40.41 1.12 2.2319 -3 1 2 4 40.63 14.44 2.2205 1 1 2 4 40.94 2.34 2.2042 0 2 2 4 41.91 2.90 2.1556 3 3 0 4 42.32 20.60 2.1356 -3 3 1 4 42.85 11.95 2.1107 -4 2 1 4 44.35 6.80 2.0427 0 4 1 4 44.82 13.26 2.0223 -4 0 2 2 45.11 7.54 2.0097 2 0 2 2 45.98 1.60 1.9738 -1 3 2 4 46.47 3.29 1.9541 -2 4 1 4 47.92 2.04 1.8983 -5 1 1 4 48.97 4.63 1.8602 3 3 1 4 49.48 1.09 1.8420 -4 2 2 4 49.76 1.19 1.8325 2 2 2 4 50.24 1.04 1.8162 1 3 2 4 50.69 2.10 1.8008 2 4 1 4 51.49 3.54 1.7749 4 2 1 4 52.15 14.31 1.7540 1 5 0 4 53.44 2.40 1.7144 3 1 2 4 54.80 6.45 1.6751 0 4 2 4 55.14 1.24 1.6656 -3 1 3 4 56.43 16.49 1.6306 -2 2 3 4 56.57 14.06 1.6268 -5 3 1 4 56.96 6.21 1.6167 4 4 0 4 59.09 4.73 1.5633 6 0 0 2 59.63 5.42 1.5505 3 5 0 4 60.37 4.94 1.5333 -6 0 2 2 60.62 3.09 1.5276 -6 2 1 4 60.77 5.63 1.5241 4 0 2 2 61.48 11.93 1.5082 -1 3 3 4 61.73 1.47 1.5028 -4 2 3 4 62.41 4.73 1.4879 0 6 0 2 62.85 1.03 1.4786 -1 5 2 4 63.11 1.56 1.4731 -3 3 3 4 64.01 1.22 1.4547 -5 1 3 4 64.62 1.59 1.4424 4 2 2 4 65.63 15.79 1.4226 5 3 1 4 66.21 9.22 1.4116 -3 5 2 4 66.36 4.10 1.4087 1 5 2 4 66.76 1.01 1.4012 1 3 3 4 67.22 4.89 1.3927 2 2 3 4 68.04 1.98 1.3779 -2 4 3 4 70.64 6.86 1.3334 -7 1 2 4 71.04 3.64 1.3268 6 2 1 4 71.15 2.06 1.3251 7 1 0 4 71.40 4.06 1.3211 -5 3 3 4 73.19 4.30 1.2932 -3 1 4 4 73.78 1.12 1.2843 -2 6 2 4 73.85 7.09 1.2832 0 6 2 4 74.64 2.07 1.2716 -4 0 4 2 74.93 3.68 1.2674 0 0 4 2 75.54 1.07 1.2587 4 4 2 4 76.25 7.10 1.2487 3 5 2 4 77.10 1.68 1.2371 -1 7 1 4 78.72 2.48 1.2157 1 7 1 4 81.95 1.38 1.1756 -8 2 1 4 82.22 1.55 1.1725 8 0 0 2 83.96 2.75 1.1525 -6 0 4 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.