Diopside Nazzareni S, Molin G, Skogby H, Dal Negro A European Journal of Mineralogy 16 (2004) 443-449 Crystal chemistry of Ti3+-Ti4+-bearing synthetic diopsides Sample: Di64 _database_code_amcsd 0007068 CELL PARAMETERS: 9.7480 8.9260 5.2640 90.000 105.890 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 440.523 Density (g/cm3): 3.258 MAX. ABS. INTENSITY / VOLUME**2: 11.80456088 RIR: 1.180 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.89 4.19 4.4630 0 2 0 2 24.29 1.51 3.6643 1 1 1 4 26.63 9.78 3.3479 0 2 1 4 27.60 22.75 3.2324 2 2 0 4 29.86 100.00 2.9927 -2 2 1 4 30.30 28.29 2.9496 3 1 0 4 30.89 32.77 2.8947 -3 1 1 4 34.96 23.72 2.5665 -1 3 1 4 35.39 2.09 2.5366 -2 0 2 2 35.46 40.64 2.5314 0 0 2 2 35.67 40.77 2.5174 2 2 1 4 37.62 1.14 2.3912 1 3 1 4 39.12 15.57 2.3029 3 1 1 4 40.65 10.10 2.2192 1 1 2 4 40.99 8.56 2.2019 0 2 2 4 41.92 8.99 2.1549 3 3 0 4 42.37 18.13 2.1332 -3 3 1 4 42.91 8.69 2.1077 -4 2 1 4 44.36 17.83 2.0420 0 4 1 4 44.94 11.37 2.0171 -4 0 2 2 45.12 7.02 2.0093 2 0 2 2 46.04 6.80 1.9714 -1 3 2 4 48.97 2.11 1.8603 3 3 1 4 49.68 6.00 1.8351 5 1 0 4 49.77 2.71 1.8321 2 2 2 4 50.26 3.26 1.8153 1 3 2 4 51.48 1.05 1.7750 4 2 1 4 52.16 13.05 1.7537 1 5 0 4 53.23 1.58 1.7209 -5 1 2 4 54.49 1.33 1.6840 -1 5 1 4 54.84 4.90 1.6740 0 4 2 4 55.29 5.66 1.6615 -3 1 3 4 56.55 16.73 1.6273 -2 2 3 4 56.64 13.68 1.6250 -5 3 1 4 56.98 5.25 1.6162 4 4 0 4 58.15 1.73 1.5864 5 3 0 4 59.12 3.60 1.5626 6 0 0 2 59.65 4.43 1.5501 3 5 0 4 60.51 4.88 1.5300 -6 0 2 2 60.70 2.29 1.5258 -6 2 1 4 60.76 6.05 1.5243 4 0 2 2 61.36 1.17 1.5109 -5 3 2 4 61.58 12.59 1.5061 -1 3 3 4 62.17 1.51 1.4932 2 4 2 4 62.42 4.48 1.4877 0 6 0 2 63.66 1.30 1.4618 4 4 1 4 64.37 2.29 1.4473 -6 2 2 4 64.61 1.49 1.4425 4 2 2 4 65.38 1.87 1.4273 0 6 1 4 65.62 17.38 1.4227 5 3 1 4 66.29 8.91 1.4100 -3 5 2 4 66.38 3.88 1.4082 1 5 2 4 67.26 4.25 1.3921 2 2 3 4 68.15 1.27 1.3759 -2 4 3 4 68.16 1.02 1.3759 -7 1 1 4 69.88 1.38 1.3460 0 4 3 4 70.79 6.52 1.3309 -7 1 2 4 71.04 3.83 1.3269 6 2 1 4 71.07 1.03 1.3264 5 1 2 4 71.19 1.18 1.3245 7 1 0 4 71.58 3.11 1.3182 -5 3 3 4 73.38 3.71 1.2902 -3 1 4 4 73.47 1.85 1.2889 -1 1 4 4 73.85 3.33 1.2833 -2 6 2 4 73.89 5.98 1.2826 0 6 2 4 74.87 1.67 1.2683 -4 0 4 2 75.05 3.26 1.2657 0 0 4 2 75.36 1.42 1.2612 -7 3 1 4 76.26 7.06 1.2486 3 5 2 4 77.13 1.28 1.2367 -1 7 1 4 78.73 2.08 1.2154 1 7 1 4 82.27 1.65 1.1719 8 0 0 2 84.24 3.11 1.1494 -6 0 4 2 88.02 1.50 1.1096 2 2 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.