Diopside Nazzareni S, Molin G, Skogby H, Dal Negro A European Journal of Mineralogy 16 (2004) 443-449 Crystal chemistry of Ti3+-Ti4+-bearing synthetic diopsides Sample: Di73* _database_code_amcsd 0007073 CELL PARAMETERS: 9.7650 8.9290 5.2840 90.000 106.190 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 442.450 Density (g/cm3): 3.232 MAX. ABS. INTENSITY / VOLUME**2: 11.51771283 RIR: 1.160 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.89 4.90 4.4645 0 2 0 2 24.29 1.11 3.6645 1 1 1 4 26.59 12.04 3.3519 0 2 1 4 27.59 22.82 3.2333 2 2 0 4 29.77 100.00 3.0008 -2 2 1 4 30.29 29.28 2.9503 3 1 0 4 30.79 33.03 2.9042 -3 1 1 4 34.91 23.02 2.5703 -1 3 1 4 35.21 2.68 2.5486 -2 0 2 2 35.38 40.34 2.5372 0 0 2 2 35.68 40.04 2.5163 2 2 1 4 37.61 1.27 2.3918 1 3 1 4 39.15 15.44 2.3010 3 1 1 4 40.62 10.09 2.2212 1 1 2 4 40.91 8.20 2.2059 0 2 2 4 41.91 8.49 2.1555 3 3 0 4 42.29 16.61 2.1373 -3 3 1 4 42.81 7.99 2.1126 -4 2 1 4 44.33 18.53 2.0433 0 4 1 4 44.72 10.82 2.0264 -4 0 2 2 45.12 6.13 2.0093 2 0 2 2 45.93 6.35 1.9758 -1 3 2 4 46.44 1.01 1.9553 -2 4 1 4 48.99 1.64 1.8595 3 3 1 4 49.67 6.33 1.8355 5 1 0 4 49.76 2.77 1.8323 2 2 2 4 50.22 2.97 1.8166 1 3 2 4 52.14 12.00 1.7543 1 5 0 4 53.00 1.73 1.7278 -5 1 2 4 54.44 1.20 1.6854 -1 5 1 4 54.77 4.99 1.6759 0 4 2 4 55.01 5.66 1.6691 -3 1 3 4 56.33 16.29 1.6333 -2 2 3 4 56.54 13.79 1.6278 -5 3 1 4 56.96 5.19 1.6166 4 4 0 4 58.14 1.62 1.5868 5 3 0 4 59.11 3.34 1.5630 6 0 0 2 59.63 4.37 1.5506 3 5 0 4 60.27 4.75 1.5356 -6 0 2 2 60.58 2.04 1.5284 -6 2 1 4 60.81 5.81 1.5232 4 0 2 2 61.15 1.06 1.5156 -5 3 2 4 61.40 12.34 1.5099 -1 3 3 4 62.16 1.49 1.4934 2 4 2 4 62.40 4.50 1.4882 0 6 0 2 63.68 1.19 1.4612 4 4 1 4 64.13 2.15 1.4521 -6 2 2 4 64.66 1.53 1.4416 4 2 2 4 65.35 1.78 1.4280 0 6 1 4 65.66 16.92 1.4219 5 3 1 4 66.14 8.78 1.4129 -3 5 2 4 66.34 3.40 1.4090 1 5 2 4 67.21 4.17 1.3928 2 2 3 4 67.94 1.34 1.3796 -2 4 3 4 69.76 1.36 1.3482 0 4 3 4 70.54 6.50 1.3351 -7 1 2 4 71.09 3.51 1.3261 6 2 1 4 71.14 1.11 1.3253 5 1 2 4 71.17 1.20 1.3248 7 1 0 4 71.25 3.04 1.3235 -5 3 3 4 73.02 3.77 1.2957 -3 1 4 4 73.22 1.82 1.2927 -1 1 4 4 73.72 3.33 1.2851 -2 6 2 4 73.82 5.93 1.2837 0 6 2 4 74.45 1.56 1.2743 -4 0 4 2 74.84 3.11 1.2686 0 0 4 2 75.23 1.52 1.2630 -7 3 1 4 76.27 6.75 1.2485 3 5 2 4 77.07 1.21 1.2374 -1 7 1 4 78.70 1.89 1.2158 1 7 1 4 82.24 1.45 1.1722 8 0 0 2 83.73 2.98 1.1551 -6 0 4 2 87.92 1.39 1.1106 2 2 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.