LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 250 K _database_code_amcsd 0007308 CELL PARAMETERS: 9.5277 8.5722 5.2512 90.000 109.990 90.000 SPACE GROUP: P2_1/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 403.044 Density (g/cm3): 3.771 MAX. ABS. INTENSITY / VOLUME**2: 20.63018306 RIR: 1.782 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.30 82.00 6.1919 1 1 0 4 19.83 4.20 4.4768 2 0 0 2 20.19 45.44 4.3992 -1 1 1 4 20.72 30.81 4.2861 0 2 0 2 25.60 38.65 3.4790 1 1 1 4 30.24 100.00 2.9560 -2 2 1 4 31.75 65.96 2.8186 3 1 0 4 32.90 8.65 2.7221 1 3 0 4 35.85 6.32 2.5048 -1 1 2 4 35.98 22.50 2.4958 -1 3 1 4 36.41 33.22 2.4674 0 0 2 2 37.78 29.94 2.3814 2 2 1 4 39.43 2.87 2.2852 1 3 1 4 40.05 3.44 2.2514 -3 1 2 4 41.03 2.42 2.1996 -2 2 2 4 41.14 1.12 2.1944 1 0 2 2 42.17 2.86 2.1430 0 4 0 2 42.53 19.39 2.1258 1 1 2 4 43.34 20.16 2.0879 -3 3 1 4 43.71 10.97 2.0709 -4 2 1 4 44.38 9.30 2.0411 -4 0 2 2 46.18 1.23 1.9657 0 4 1 4 47.01 2.05 1.9330 2 4 0 4 47.79 5.12 1.9033 2 0 2 2 47.94 14.49 1.8975 -2 4 1 4 48.98 8.06 1.8597 -5 1 1 4 49.46 3.45 1.8428 -4 2 2 4 50.50 2.98 1.8073 -3 3 2 4 51.90 1.87 1.7616 3 3 1 4 53.40 4.17 1.7159 2 4 1 4 54.20 1.33 1.6922 -1 1 3 4 54.49 8.30 1.6838 1 5 0 4 54.85 4.50 1.6737 4 2 1 4 56.83 18.16 1.6200 -2 2 3 4 56.91 9.20 1.6180 0 4 2 4 56.99 10.04 1.6159 3 1 2 4 58.08 2.45 1.5881 -4 4 1 4 58.20 17.86 1.5851 -5 3 1 4 59.74 8.34 1.5480 4 4 0 4 60.55 4.39 1.5292 -6 0 2 2 61.35 1.05 1.5112 -4 2 3 4 61.67 3.50 1.5040 1 1 3 4 61.81 2.70 1.5009 5 1 1 4 62.21 3.88 1.4923 6 0 0 2 62.41 2.51 1.4879 -6 2 1 4 62.47 6.11 1.4866 3 5 0 4 62.88 2.75 1.4780 -4 4 2 4 62.90 9.37 1.4775 -1 3 3 4 63.27 4.08 1.4698 -5 1 3 4 63.43 2.68 1.4664 -3 3 3 4 65.02 1.87 1.4344 -1 5 2 4 65.14 2.99 1.4320 4 0 2 2 65.31 6.82 1.4287 0 6 0 2 67.57 1.17 1.3864 4 4 1 4 67.83 7.67 1.3816 -3 5 2 4 69.16 2.01 1.3582 4 2 2 4 69.33 6.37 1.3554 -2 4 3 4 69.74 1.81 1.3485 -2 6 1 4 69.81 3.05 1.3472 1 3 3 4 69.94 15.51 1.3450 5 3 1 4 70.95 3.61 1.3283 2 2 3 4 71.32 4.01 1.3225 -5 3 3 4 71.36 9.55 1.3217 -7 1 2 4 73.13 4.37 1.2940 -3 1 4 4 73.97 3.83 1.2814 -4 0 4 2 75.09 2.91 1.2651 7 1 0 4 75.97 1.94 1.2526 6 2 1 4 76.53 1.51 1.2448 -6 4 2 4 77.15 8.07 1.2364 0 6 2 4 77.35 2.10 1.2337 0 0 4 2 79.60 1.10 1.2043 4 6 0 4 80.67 1.82 1.1911 -1 7 1 4 80.70 1.10 1.1907 4 4 2 4 80.99 6.50 1.1871 3 5 2 4 82.39 1.21 1.1704 -4 6 2 4 82.72 2.21 1.1667 -6 0 4 2 82.80 2.47 1.1658 1 7 1 4 84.86 1.19 1.1426 2 6 2 4 85.14 1.06 1.1396 -8 -2 1 4 89.01 1.20 1.0998 -4 4 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.