LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 265 K _database_code_amcsd 0007309 CELL PARAMETERS: 9.5267 8.5688 5.2553 90.000 110.060 90.000 SPACE GROUP: P2_1/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 402.977 Density (g/cm3): 3.771 MAX. ABS. INTENSITY / VOLUME**2: 20.74679274 RIR: 1.791 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.31 81.69 6.1890 1 1 0 4 19.84 4.09 4.4744 2 0 0 2 20.17 45.06 4.4017 -1 1 1 4 20.73 30.61 4.2844 0 2 0 2 25.61 38.52 3.4779 1 1 1 4 30.23 100.00 2.9565 -2 2 1 4 31.76 65.09 2.8171 3 1 0 4 32.92 8.57 2.7210 1 3 0 4 35.83 6.45 2.5063 -1 1 2 4 35.99 21.92 2.4956 -1 3 1 4 36.40 33.38 2.4682 0 0 2 2 37.80 29.68 2.3801 2 2 1 4 39.45 2.93 2.2844 1 3 1 4 40.02 3.29 2.2532 -3 1 2 4 41.01 2.48 2.2008 -2 2 2 4 42.18 2.80 2.1422 0 4 0 2 42.53 19.48 2.1257 1 1 2 4 43.34 19.84 2.0878 -3 3 1 4 43.71 10.78 2.0708 -4 2 1 4 44.35 9.23 2.0425 -4 0 2 2 46.19 1.25 1.9651 0 4 1 4 47.03 1.97 1.9322 2 4 0 4 47.80 5.03 1.9027 2 0 2 2 47.95 14.43 1.8972 -2 4 1 4 48.99 8.03 1.8595 -5 1 1 4 49.43 3.47 1.8437 -4 2 2 4 50.48 3.01 1.8080 -3 3 2 4 51.93 1.89 1.7607 3 3 1 4 53.42 4.03 1.7151 2 4 1 4 54.17 1.34 1.6931 -1 1 3 4 54.52 8.26 1.6832 1 5 0 4 54.89 4.44 1.6726 4 2 1 4 56.80 18.07 1.6210 -2 2 3 4 56.92 9.27 1.6178 0 4 2 4 57.02 9.84 1.6152 3 1 2 4 58.09 2.42 1.5878 -4 4 1 4 58.21 17.79 1.5848 -5 3 1 4 59.77 8.29 1.5473 4 4 0 4 60.52 4.29 1.5297 -6 0 2 2 61.30 1.05 1.5123 -4 2 3 4 61.67 3.46 1.5041 1 1 3 4 61.86 2.65 1.4999 5 1 1 4 62.25 3.79 1.4915 6 0 0 2 62.43 2.48 1.4876 -6 2 1 4 62.50 5.96 1.4860 3 5 0 4 62.87 2.70 1.4782 -4 4 2 4 62.88 9.30 1.4780 -1 3 3 4 63.22 4.04 1.4709 -5 1 3 4 63.39 2.81 1.4672 -3 3 3 4 65.02 1.85 1.4344 -1 5 2 4 65.18 2.92 1.4312 4 0 2 2 65.34 6.62 1.4281 0 6 0 2 67.61 1.17 1.3856 4 4 1 4 67.83 7.72 1.3817 -3 5 2 4 69.21 2.01 1.3575 4 2 2 4 69.31 6.24 1.3558 -2 4 3 4 69.76 1.77 1.3481 -2 6 1 4 69.81 2.91 1.3472 1 3 3 4 69.99 15.19 1.3442 5 3 1 4 70.97 3.61 1.3281 2 2 3 4 71.27 3.97 1.3232 -5 3 3 4 71.35 9.49 1.3219 -7 1 2 4 73.06 4.37 1.2951 -3 1 4 4 73.89 3.83 1.2826 -4 0 4 2 75.14 2.87 1.2644 7 1 0 4 76.03 1.91 1.2517 6 2 1 4 76.52 1.48 1.2449 -6 4 2 4 77.17 8.11 1.2361 0 6 2 4 77.32 2.13 1.2341 0 0 4 2 79.65 1.11 1.2038 4 6 0 4 80.70 1.78 1.1907 -1 7 1 4 80.75 1.06 1.1901 4 4 2 4 81.03 6.45 1.1866 3 5 2 4 82.40 1.15 1.1704 -4 6 2 4 82.63 2.24 1.1677 -6 0 4 2 82.84 2.38 1.1653 1 7 1 4 84.90 1.16 1.1422 2 6 2 4 85.17 1.03 1.1393 -8 -2 1 4 88.95 1.21 1.1004 -4 4 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.