LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 363 K _database_code_amcsd 0007314 CELL PARAMETERS: 9.5646 8.5738 5.2684 90.000 110.221 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 405.407 Density (g/cm3): 3.749 MAX. ABS. INTENSITY / VOLUME**2: 21.12165958 RIR: 1.835 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.29 81.62 6.1996 1 1 0 4 19.78 3.66 4.4875 2 0 0 2 20.12 43.08 4.4128 -1 1 1 4 20.72 30.39 4.2869 0 2 0 2 25.59 37.55 3.4813 1 1 1 4 30.15 100.00 2.9640 -2 2 1 4 31.68 63.05 2.8247 3 1 0 4 32.89 8.78 2.7232 1 3 0 4 35.75 5.98 2.5116 -1 1 2 4 35.94 19.83 2.4986 -1 3 1 4 36.35 33.26 2.4718 0 0 2 2 37.76 27.75 2.3827 2 2 1 4 39.42 3.36 2.2861 1 3 1 4 39.86 2.90 2.2616 -3 1 2 4 40.90 2.86 2.2064 -2 2 2 4 42.16 2.55 2.1435 0 4 0 2 42.48 19.87 2.1279 1 1 2 4 43.23 18.76 2.0927 -3 3 1 4 43.56 10.01 2.0778 -4 2 1 4 44.15 8.91 2.0513 -4 0 2 2 46.16 1.28 1.9666 0 4 1 4 46.98 2.02 1.9341 2 4 0 4 47.75 4.51 1.9047 2 0 2 2 47.88 15.03 1.8998 -2 4 1 4 48.78 8.13 1.8667 -5 1 1 4 49.24 3.43 1.8504 -4 2 2 4 50.34 2.90 1.8127 -3 3 2 4 51.87 1.97 1.7628 3 3 1 4 52.73 1.01 1.7360 -5 1 2 4 53.37 3.60 1.7165 2 4 1 4 54.06 1.47 1.6963 -1 1 3 4 54.48 8.24 1.6843 1 5 0 4 54.79 4.13 1.6753 4 2 1 4 56.65 17.21 1.6247 -2 2 3 4 56.86 9.06 1.6194 0 4 2 4 56.95 9.55 1.6170 3 1 2 4 57.95 2.26 1.5914 -4 4 1 4 58.03 17.43 1.5895 -5 3 1 4 59.66 8.05 1.5499 4 4 0 4 60.23 3.84 1.5364 -6 0 2 2 61.07 1.05 1.5174 -4 2 3 4 61.59 3.44 1.5058 1 1 3 4 61.73 2.56 1.5028 5 1 1 4 62.04 3.50 1.4958 6 0 0 2 62.19 2.57 1.4928 -6 2 1 4 62.42 5.39 1.4877 3 5 0 4 62.69 2.65 1.4820 -4 4 2 4 62.77 9.16 1.4803 -1 3 3 4 62.93 3.82 1.4768 -5 1 3 4 63.22 3.18 1.4709 -3 3 3 4 64.94 1.89 1.4359 -1 5 2 4 65.09 2.86 1.4331 4 0 2 2 65.30 5.83 1.4290 0 6 0 2 67.51 1.19 1.3874 4 4 1 4 67.70 7.73 1.3841 -3 5 2 4 69.11 2.17 1.3591 4 2 2 4 69.17 5.75 1.3582 -2 4 3 4 69.68 1.51 1.3495 -2 6 1 4 69.73 2.54 1.3486 1 3 3 4 69.86 13.75 1.3464 5 3 1 4 70.88 3.73 1.3294 2 2 3 4 71.00 3.69 1.3276 -5 3 3 4 71.00 9.20 1.3275 -7 1 2 4 72.56 1.14 1.3028 -6 2 3 4 72.84 4.32 1.2986 -3 1 4 4 73.62 4.00 1.2867 -4 0 4 2 74.88 2.74 1.2681 7 1 0 4 75.86 1.97 1.2542 6 2 1 4 76.25 1.49 1.2488 -6 4 2 4 77.09 8.02 1.2371 0 6 2 4 77.18 2.13 1.2359 0 0 4 2 79.53 1.25 1.2053 4 6 0 4 80.63 1.74 1.1916 -1 7 1 4 80.65 1.01 1.1913 4 4 2 4 80.95 6.19 1.1876 3 5 2 4 82.22 1.10 1.1725 -4 6 2 4 82.24 2.24 1.1723 -6 0 4 2 82.77 1.96 1.1660 1 7 1 4 84.82 1.11 1.1430 2 6 2 4 88.66 1.21 1.1032 -4 4 4 4 89.93 2.37 1.0909 -7 1 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.