LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 573 K _database_code_amcsd 0007318 CELL PARAMETERS: 9.5859 8.5911 5.2731 90.000 110.173 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 407.619 Density (g/cm3): 3.728 MAX. ABS. INTENSITY / VOLUME**2: 20.95335020 RIR: 1.830 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.25 80.14 6.2136 1 1 0 4 19.73 3.50 4.4989 2 0 0 2 20.10 44.36 4.4180 -1 1 1 4 20.68 29.57 4.2955 0 2 0 2 25.54 37.36 3.4878 1 1 1 4 30.10 100.00 2.9690 -2 2 1 4 31.60 61.91 2.8317 3 1 0 4 32.82 8.90 2.7288 1 3 0 4 35.71 5.66 2.5142 -1 1 2 4 35.88 19.26 2.5030 -1 3 1 4 36.30 32.71 2.4748 0 0 2 2 37.67 27.55 2.3878 2 2 1 4 39.34 3.13 2.2906 1 3 1 4 39.81 2.95 2.2642 -3 1 2 4 40.85 2.58 2.2090 -2 2 2 4 42.07 2.63 2.1478 0 4 0 2 42.41 19.33 2.1313 1 1 2 4 43.14 17.96 2.0967 -3 3 1 4 43.47 9.89 2.0820 -4 2 1 4 44.09 8.57 2.0541 -4 0 2 2 46.07 1.33 1.9703 0 4 1 4 46.87 2.08 1.9382 2 4 0 4 47.66 4.26 1.9082 2 0 2 2 47.79 14.16 1.9034 -2 4 1 4 48.67 7.95 1.8708 -5 1 1 4 49.17 3.31 1.8531 -4 2 2 4 50.26 3.00 1.8153 -3 3 2 4 51.74 1.90 1.7667 3 3 1 4 53.25 3.37 1.7201 2 4 1 4 54.00 1.57 1.6981 -1 1 3 4 54.36 7.98 1.6877 1 5 0 4 54.65 3.99 1.6793 4 2 1 4 56.59 16.50 1.6264 -2 2 3 4 56.75 8.87 1.6221 0 4 2 4 56.82 9.00 1.6203 3 1 2 4 57.82 1.99 1.5946 -4 4 1 4 57.89 16.58 1.5929 -5 3 1 4 59.51 7.89 1.5534 4 4 0 4 60.11 3.70 1.5392 -6 0 2 2 60.99 1.02 1.5191 -4 2 3 4 61.49 3.30 1.5080 1 1 3 4 61.56 2.52 1.5065 5 1 1 4 61.87 3.30 1.4996 6 0 0 2 62.03 2.40 1.4961 -6 2 1 4 62.27 5.07 1.4909 3 5 0 4 62.57 2.65 1.4845 -4 4 2 4 62.68 8.71 1.4822 -1 3 3 4 62.85 3.65 1.4786 -5 1 3 4 63.13 2.85 1.4727 -3 3 3 4 64.82 1.69 1.4383 -1 5 2 4 64.93 2.72 1.4362 4 0 2 2 65.15 5.45 1.4318 0 6 0 2 67.34 1.02 1.3905 4 4 1 4 67.57 7.26 1.3864 -3 5 2 4 68.94 2.04 1.3621 4 2 2 4 69.06 5.20 1.3600 -2 4 3 4 69.52 1.48 1.3521 -2 6 1 4 69.60 2.26 1.3507 1 3 3 4 69.67 12.83 1.3497 5 3 1 4 70.75 3.58 1.3317 2 2 3 4 70.84 8.57 1.3301 -7 1 2 4 70.88 3.44 1.3294 -5 3 3 4 72.44 1.02 1.3047 -6 2 3 4 72.76 4.13 1.2997 -3 1 4 4 73.54 3.59 1.2879 -4 0 4 2 74.66 2.61 1.2713 7 1 0 4 75.64 1.87 1.2573 6 2 1 4 76.08 1.46 1.2511 -6 4 2 4 76.93 7.31 1.2394 0 6 2 4 77.07 2.02 1.2374 0 0 4 2 79.32 1.08 1.2079 4 6 0 4 80.44 1.02 1.1939 4 4 2 4 80.44 1.70 1.1939 -1 7 1 4 80.75 5.68 1.1901 3 5 2 4 82.13 2.06 1.1736 -6 0 4 2 82.57 1.86 1.1684 1 7 1 4 88.53 1.16 1.1045 -4 4 4 4 89.79 2.12 1.0922 -7 1 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.