LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 673 K _database_code_amcsd 0007319 CELL PARAMETERS: 9.5942 8.6018 5.2752 90.000 110.169 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 408.653 Density (g/cm3): 3.719 MAX. ABS. INTENSITY / VOLUME**2: 20.84412958 RIR: 1.825 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.24 80.04 6.2203 1 1 0 4 19.72 3.33 4.5029 2 0 0 2 20.09 45.23 4.4209 -1 1 1 4 20.65 29.47 4.3009 0 2 0 2 25.52 37.17 3.4902 1 1 1 4 30.07 100.00 2.9717 -2 2 1 4 31.57 61.35 2.8343 3 1 0 4 32.78 8.88 2.7321 1 3 0 4 35.70 5.52 2.5154 -1 1 2 4 35.84 19.07 2.5056 -1 3 1 4 36.28 32.35 2.4759 0 0 2 2 37.64 27.50 2.3898 2 2 1 4 39.29 3.02 2.2929 1 3 1 4 39.79 2.97 2.2655 -3 1 2 4 40.82 2.41 2.2105 -2 2 2 4 42.02 2.68 2.1504 0 4 0 2 42.39 19.02 2.1325 1 1 2 4 43.10 17.54 2.0989 -3 3 1 4 43.42 9.81 2.0839 -4 2 1 4 44.06 8.39 2.0554 -4 0 2 2 46.01 1.39 1.9725 0 4 1 4 46.82 2.14 1.9405 2 4 0 4 47.63 4.16 1.9093 2 0 2 2 47.73 13.81 1.9055 -2 4 1 4 48.63 7.85 1.8724 -5 1 1 4 49.13 3.25 1.8545 -4 2 2 4 50.22 3.02 1.8168 -3 3 2 4 51.69 1.83 1.7684 3 3 1 4 53.19 3.28 1.7219 2 4 1 4 53.98 1.63 1.6988 -1 1 3 4 54.29 7.83 1.6898 1 5 0 4 54.60 3.90 1.6808 4 2 1 4 56.56 16.16 1.6272 -2 2 3 4 56.70 8.78 1.6235 0 4 2 4 56.78 8.70 1.6214 3 1 2 4 57.76 1.90 1.5963 -4 4 1 4 57.83 16.12 1.5945 -5 3 1 4 59.44 7.75 1.5551 4 4 0 4 60.06 3.61 1.5404 -6 0 2 2 61.46 3.22 1.5088 1 1 3 4 61.50 2.53 1.5078 5 1 1 4 61.81 3.21 1.5010 6 0 0 2 61.97 2.31 1.4975 -6 2 1 4 62.19 4.93 1.4926 3 5 0 4 62.51 2.66 1.4859 -4 4 2 4 62.64 8.44 1.4831 -1 3 3 4 62.81 3.55 1.4795 -5 1 3 4 63.09 2.68 1.4736 -3 3 3 4 64.75 1.59 1.4398 -1 5 2 4 64.88 2.65 1.4372 4 0 2 2 65.06 5.26 1.4336 0 6 0 2 67.49 7.03 1.3878 -3 5 2 4 68.88 1.97 1.3631 4 2 2 4 69.00 4.98 1.3610 -2 4 3 4 69.43 1.46 1.3537 -2 6 1 4 69.55 2.14 1.3516 1 3 3 4 69.59 12.35 1.3509 5 3 1 4 70.70 3.49 1.3325 2 2 3 4 70.78 8.26 1.3312 -7 1 2 4 70.83 3.33 1.3304 -5 3 3 4 72.72 4.05 1.3003 -3 1 4 4 73.50 3.39 1.2884 -4 0 4 2 74.58 2.56 1.2724 7 1 0 4 75.56 1.82 1.2584 6 2 1 4 75.99 1.45 1.2523 -6 4 2 4 76.83 6.96 1.2407 0 6 2 4 77.03 1.96 1.2379 0 0 4 2 79.21 1.01 1.2093 4 6 0 4 80.32 1.67 1.1953 -1 7 1 4 80.36 1.02 1.1949 4 4 2 4 80.66 5.46 1.1912 3 5 2 4 82.07 1.96 1.1742 -6 0 4 2 82.45 1.80 1.1698 1 7 1 4 88.46 1.14 1.1052 -4 4 4 4 89.72 2.00 1.0929 -7 1 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.