LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 773 K _database_code_amcsd 0007320 CELL PARAMETERS: 9.5997 8.6121 5.2763 90.000 110.130 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 409.564 Density (g/cm3): 3.711 MAX. ABS. INTENSITY / VOLUME**2: 20.67198318 RIR: 1.814 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.22 79.92 6.2267 1 1 0 4 19.70 3.32 4.5066 2 0 0 2 20.08 46.25 4.4227 -1 1 1 4 20.63 29.51 4.3060 0 2 0 2 25.50 37.07 3.4931 1 1 1 4 30.05 100.00 2.9737 -2 2 1 4 31.54 61.18 2.8368 3 1 0 4 32.74 8.96 2.7353 1 3 0 4 35.68 5.39 2.5162 -1 1 2 4 35.80 19.05 2.5080 -1 3 1 4 36.27 32.13 2.4770 0 0 2 2 37.60 27.48 2.3922 2 2 1 4 39.25 2.94 2.2953 1 3 1 4 39.78 2.97 2.2659 -3 1 2 4 40.81 2.25 2.2114 -2 2 2 4 41.96 2.68 2.1530 0 4 0 2 42.36 18.79 2.1339 1 1 2 4 43.06 17.25 2.1006 -3 3 1 4 43.39 9.81 2.0853 -4 2 1 4 44.05 8.29 2.0558 -4 0 2 2 45.96 1.45 1.9746 0 4 1 4 46.76 2.18 1.9427 2 4 0 4 47.59 4.06 1.9108 2 0 2 2 47.68 13.48 1.9073 -2 4 1 4 48.60 7.75 1.8735 -5 1 1 4 49.11 3.22 1.8552 -4 2 2 4 50.19 3.05 1.8178 -3 3 2 4 51.63 1.78 1.7702 3 3 1 4 53.13 3.21 1.7238 2 4 1 4 53.96 1.67 1.6994 -1 1 3 4 54.22 7.74 1.6918 1 5 0 4 54.54 3.83 1.6824 4 2 1 4 56.54 15.86 1.6278 -2 2 3 4 56.64 8.65 1.6250 0 4 2 4 56.73 8.52 1.6228 3 1 2 4 57.70 1.82 1.5977 -4 4 1 4 57.78 15.77 1.5957 -5 3 1 4 59.37 7.65 1.5567 4 4 0 4 60.04 3.54 1.5409 -6 0 2 2 61.41 3.16 1.5097 1 1 3 4 61.44 2.52 1.5092 5 1 1 4 61.75 3.13 1.5022 6 0 0 2 61.92 2.26 1.4985 -6 2 1 4 62.12 4.81 1.4943 3 5 0 4 62.46 2.63 1.4869 -4 4 2 4 62.60 8.21 1.4839 -1 3 3 4 62.80 3.44 1.4797 -5 1 3 4 63.06 2.56 1.4742 -3 3 3 4 64.68 1.51 1.4411 -1 5 2 4 64.81 2.61 1.4385 4 0 2 2 64.97 5.10 1.4353 0 6 0 2 67.43 6.85 1.3890 -3 5 2 4 68.81 1.92 1.3644 4 2 2 4 68.96 4.78 1.3618 -2 4 3 4 69.34 1.44 1.3551 -2 6 1 4 69.50 2.06 1.3526 1 3 3 4 69.52 11.98 1.3522 5 3 1 4 70.64 3.42 1.3335 2 2 3 4 70.74 8.00 1.3318 -7 1 2 4 70.80 3.25 1.3309 -5 3 3 4 72.71 3.97 1.3005 -3 1 4 4 73.49 3.23 1.2886 -4 0 4 2 74.51 2.48 1.2735 7 1 0 4 75.47 1.77 1.2596 6 2 1 4 75.94 1.43 1.2531 -6 4 2 4 76.74 6.68 1.2419 0 6 2 4 76.99 1.92 1.2385 0 0 4 2 80.21 1.62 1.1967 -1 7 1 4 80.26 1.00 1.1961 4 4 2 4 80.56 5.27 1.1924 3 5 2 4 82.06 1.88 1.1743 -6 0 4 2 82.34 1.74 1.1711 1 7 1 4 84.40 1.58 1.1477 -8 2 1 4 88.41 1.11 1.1057 -4 4 4 4 89.70 1.88 1.0931 -7 1 4 4 89.81 1.68 1.0921 -8 2 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.