LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 873 K _database_code_amcsd 0007321 CELL PARAMETERS: 9.6080 8.6219 5.2778 90.000 110.119 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 410.530 Density (g/cm3): 3.702 MAX. ABS. INTENSITY / VOLUME**2: 20.54220691 RIR: 1.807 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.21 80.17 6.2332 1 1 0 4 19.68 3.23 4.5109 2 0 0 2 20.07 46.42 4.4251 -1 1 1 4 20.60 29.34 4.3109 0 2 0 2 25.48 37.17 3.4955 1 1 1 4 30.03 100.00 2.9762 -2 2 1 4 31.51 61.06 2.8395 3 1 0 4 32.70 8.96 2.7384 1 3 0 4 35.67 5.32 2.5171 -1 1 2 4 35.77 19.03 2.5103 -1 3 1 4 36.25 31.74 2.4779 0 0 2 2 37.57 27.49 2.3943 2 2 1 4 39.21 2.85 2.2974 1 3 1 4 39.76 3.01 2.2670 -3 1 2 4 40.78 2.15 2.2125 -2 2 2 4 41.91 2.69 2.1555 0 4 0 2 42.33 18.55 2.1350 1 1 2 4 43.02 16.99 2.1026 -3 3 1 4 43.35 9.72 2.0871 -4 2 1 4 44.02 8.21 2.0569 -4 0 2 2 45.91 1.44 1.9766 0 4 1 4 46.71 2.19 1.9448 2 4 0 4 47.56 4.02 1.9119 2 0 2 2 47.63 13.17 1.9093 -2 4 1 4 48.55 7.67 1.8752 -5 1 1 4 49.07 3.10 1.8564 -4 2 2 4 50.15 3.14 1.8191 -3 3 2 4 51.58 1.72 1.7719 3 3 1 4 53.07 3.17 1.7255 2 4 1 4 53.94 1.66 1.7000 -1 1 3 4 54.15 7.62 1.6937 1 5 0 4 54.49 3.74 1.6839 4 2 1 4 56.51 15.61 1.6285 -2 2 3 4 56.59 8.62 1.6263 0 4 2 4 56.68 8.28 1.6239 3 1 2 4 57.64 1.72 1.5993 -4 4 1 4 57.72 15.48 1.5972 -5 3 1 4 59.30 7.58 1.5583 4 4 0 4 59.99 3.44 1.5421 -6 0 2 2 61.38 2.48 1.5105 5 1 1 4 61.38 3.05 1.5104 1 1 3 4 61.69 3.03 1.5036 6 0 0 2 61.86 2.22 1.4999 -6 2 1 4 62.04 4.65 1.4959 3 5 0 4 62.40 2.62 1.4881 -4 4 2 4 62.56 8.07 1.4847 -1 3 3 4 62.76 3.39 1.4804 -5 1 3 4 63.02 2.42 1.4750 -3 3 3 4 64.62 1.44 1.4423 -1 5 2 4 64.76 2.60 1.4396 4 0 2 2 64.89 4.98 1.4370 0 6 0 2 67.36 6.61 1.3902 -3 5 2 4 68.75 1.84 1.3654 4 2 2 4 68.91 4.59 1.3627 -2 4 3 4 69.26 1.43 1.3566 -2 6 1 4 69.44 11.67 1.3535 5 3 1 4 69.45 1.99 1.3534 1 3 3 4 70.59 3.35 1.3342 2 2 3 4 70.68 7.76 1.3328 -7 1 2 4 70.75 3.17 1.3317 -5 3 3 4 72.68 3.88 1.3009 -3 1 4 4 73.47 3.12 1.2890 -4 0 4 2 74.43 2.43 1.2747 7 1 0 4 75.39 1.73 1.2607 6 2 1 4 75.86 1.39 1.2542 -6 4 2 4 76.66 6.43 1.2431 0 6 2 4 76.96 1.86 1.2389 0 0 4 2 80.11 1.57 1.1980 -1 7 1 4 80.47 5.06 1.1935 3 5 2 4 82.02 1.79 1.1748 -6 0 4 2 82.23 1.70 1.1724 1 7 1 4 84.30 1.51 1.1488 -8 2 1 4 88.35 1.07 1.1063 -4 4 4 4 89.65 1.81 1.0936 -7 1 4 4 89.73 1.62 1.0928 -8 2 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.