LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 973 K _database_code_amcsd 0007322 CELL PARAMETERS: 9.6173 8.6313 5.2804 90.000 110.118 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 411.581 Density (g/cm3): 3.692 MAX. ABS. INTENSITY / VOLUME**2: 20.52858517 RIR: 1.810 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.19 78.95 6.2396 1 1 0 4 19.66 3.13 4.5153 2 0 0 2 20.05 46.95 4.4281 -1 1 1 4 20.58 28.91 4.3156 0 2 0 2 25.46 36.91 3.4980 1 1 1 4 30.00 100.00 2.9789 -2 2 1 4 31.48 60.18 2.8423 3 1 0 4 32.67 9.03 2.7413 1 3 0 4 35.65 5.13 2.5184 -1 1 2 4 35.73 18.56 2.5127 -1 3 1 4 36.23 31.39 2.4791 0 0 2 2 37.53 27.22 2.3963 2 2 1 4 39.18 2.77 2.2996 1 3 1 4 39.73 3.00 2.2686 -3 1 2 4 40.75 2.01 2.2141 -2 2 2 4 41.86 2.72 2.1578 0 4 0 2 42.31 18.25 2.1363 1 1 2 4 42.97 16.55 2.1047 -3 3 1 4 43.31 9.62 2.0892 -4 2 1 4 43.99 8.07 2.0585 -4 0 2 2 45.86 1.50 1.9786 0 4 1 4 46.65 2.24 1.9469 2 4 0 4 47.53 3.88 1.9132 2 0 2 2 47.58 12.80 1.9112 -2 4 1 4 48.50 7.59 1.8770 -5 1 1 4 49.03 3.05 1.8580 -4 2 2 4 50.10 3.16 1.8206 -3 3 2 4 51.53 1.71 1.7735 3 3 1 4 53.02 2.99 1.7272 2 4 1 4 53.91 1.72 1.7008 -1 1 3 4 54.09 7.50 1.6956 1 5 0 4 54.44 3.67 1.6854 4 2 1 4 56.48 15.20 1.6294 -2 2 3 4 56.54 8.48 1.6276 0 4 2 4 56.64 8.00 1.6251 3 1 2 4 57.57 1.58 1.6009 -4 4 1 4 57.66 15.06 1.5988 -5 3 1 4 59.24 7.48 1.5599 4 4 0 4 59.93 3.38 1.5434 -6 0 2 2 61.31 2.45 1.5119 5 1 1 4 61.34 2.98 1.5112 1 1 3 4 61.62 2.96 1.5051 6 0 0 2 61.79 2.14 1.5014 -6 2 1 4 61.97 4.52 1.4975 3 5 0 4 62.34 2.59 1.4894 -4 4 2 4 62.52 7.87 1.4857 -1 3 3 4 62.71 3.28 1.4815 -5 1 3 4 62.97 2.28 1.4760 -3 3 3 4 64.55 1.36 1.4437 -1 5 2 4 64.70 2.53 1.4407 4 0 2 2 64.81 4.77 1.4385 0 6 0 2 67.29 6.44 1.3915 -3 5 2 4 68.69 1.78 1.3665 4 2 2 4 68.85 4.33 1.3637 -2 4 3 4 69.18 1.39 1.3580 -2 6 1 4 69.37 11.18 1.3547 5 3 1 4 69.40 1.86 1.3543 1 3 3 4 70.54 3.29 1.3351 2 2 3 4 70.60 7.47 1.3340 -7 1 2 4 70.68 3.04 1.3327 -5 3 3 4 72.64 3.80 1.3016 -3 1 4 4 73.42 2.94 1.2897 -4 0 4 2 74.34 2.35 1.2759 7 1 0 4 75.31 1.69 1.2619 6 2 1 4 75.77 1.37 1.2553 -6 4 2 4 76.57 6.12 1.2442 0 6 2 4 76.91 1.82 1.2396 0 0 4 2 80.01 1.57 1.1993 -1 7 1 4 80.39 4.84 1.1945 3 5 2 4 81.95 1.72 1.1756 -6 0 4 2 82.12 1.63 1.1736 1 7 1 4 84.20 1.46 1.1499 -8 2 1 4 88.28 1.04 1.1070 -4 4 4 4 89.57 1.69 1.0944 -7 1 4 4 89.63 1.56 1.0938 -8 2 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.