LiGaSi2O6 Camara F, Nestola F, Angel R J, Ohashi H European Journal of Mineralogy 21 (2009) 599-614 Spontaneous strain variations through the low-temperature displacive phase transition of LiGaSi2O6 clinopyroxene Locality: synthetic Note: T = 1073 K _database_code_amcsd 0007323 CELL PARAMETERS: 9.6260 8.6433 5.2813 90.000 110.098 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 412.649 Density (g/cm3): 3.683 MAX. ABS. INTENSITY / VOLUME**2: 20.35946838 RIR: 1.800 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.18 79.03 6.2472 1 1 0 4 19.64 2.94 4.5199 2 0 0 2 20.04 47.98 4.4304 -1 1 1 4 20.55 28.83 4.3217 0 2 0 2 25.44 36.89 3.5006 1 1 1 4 29.97 100.00 2.9816 -2 2 1 4 31.44 60.15 2.8453 3 1 0 4 32.62 9.05 2.7451 1 3 0 4 35.64 5.09 2.5192 -1 1 2 4 35.69 18.76 2.5155 -1 3 1 4 36.22 31.15 2.4799 0 0 2 2 37.49 27.46 2.3987 2 2 1 4 39.13 2.63 2.3021 1 3 1 4 39.72 3.05 2.2695 -3 1 2 4 40.73 1.92 2.2152 -2 2 2 4 41.80 2.78 2.1608 0 4 0 2 42.28 18.02 2.1374 1 1 2 4 42.93 16.33 2.1069 -3 3 1 4 43.27 9.67 2.0912 -4 2 1 4 43.97 8.00 2.0594 -4 0 2 2 45.80 1.54 1.9810 0 4 1 4 46.59 2.31 1.9495 2 4 0 4 47.50 3.83 1.9143 2 0 2 2 47.52 12.46 1.9135 -2 4 1 4 48.45 7.59 1.8787 -5 1 1 4 49.00 3.00 1.8591 -4 2 2 4 50.06 3.23 1.8220 -3 3 2 4 51.47 1.64 1.7754 3 3 1 4 52.95 3.03 1.7292 2 4 1 4 53.89 1.75 1.7013 -1 1 3 4 54.01 7.41 1.6979 1 5 0 4 54.38 3.63 1.6872 4 2 1 4 56.45 15.06 1.6300 -2 2 3 4 56.49 8.50 1.6291 0 4 2 4 56.59 7.81 1.6263 3 1 2 4 57.50 1.54 1.6027 -4 4 1 4 57.59 14.68 1.6004 -5 3 1 4 59.16 7.43 1.5618 4 4 0 4 59.89 3.34 1.5445 -6 0 2 2 61.25 2.49 1.5134 5 1 1 4 61.31 2.95 1.5119 1 1 3 4 61.55 2.93 1.5066 6 0 0 2 61.72 2.08 1.5029 -6 2 1 4 61.88 4.41 1.4994 3 5 0 4 62.28 2.60 1.4908 -4 4 2 4 62.48 7.68 1.4864 -1 3 3 4 62.69 3.27 1.4821 -5 1 3 4 62.94 2.16 1.4768 -3 3 3 4 64.48 1.28 1.4451 -1 5 2 4 64.64 2.48 1.4418 4 0 2 2 64.71 4.69 1.4405 0 6 0 2 67.21 6.28 1.3929 -3 5 2 4 68.62 1.75 1.3677 4 2 2 4 68.80 4.21 1.3646 -2 4 3 4 69.07 1.42 1.3598 -2 6 1 4 69.28 10.98 1.3562 5 3 1 4 69.35 1.78 1.3551 1 3 3 4 70.49 3.23 1.3359 2 2 3 4 70.54 7.30 1.3351 -7 1 2 4 70.64 2.98 1.3335 -5 3 3 4 72.62 3.77 1.3019 -3 1 4 4 73.40 2.82 1.2899 -4 0 4 2 74.25 2.34 1.2772 7 1 0 4 75.22 1.65 1.2632 6 2 1 4 75.69 1.37 1.2565 -6 4 2 4 76.47 5.94 1.2456 0 6 2 4 76.89 1.79 1.2399 0 0 4 2 79.88 1.52 1.2009 -1 7 1 4 80.29 4.72 1.1958 3 5 2 4 81.92 1.66 1.1760 -6 0 4 2 81.99 1.62 1.1752 1 7 1 4 84.09 1.41 1.1511 -8 2 1 4 88.22 1.04 1.1076 -4 4 4 4 89.52 1.63 1.0948 -7 1 4 4 89.55 1.54 1.0945 -8 2 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.