Co(OD)2 Parise J B, Theroux B, Li R, Loveday J S, Marshall W G, Klotz S Physics and Chemistry of Minerals 25 (1998) 130-137 Pressure dependence of hydrogen bonding in metal deuteroxides: a neutron powder diffraction study of Mn(OD)2 and beta-Co(OD)2. Sample: P = 0.0 GPa _database_code_amcsd 0008117 CELL PARAMETERS: 3.1834 3.1834 4.6445 90.000 90.000 120.000 SPACE GROUP: P-3m1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 40.762 Density (g/cm3): 3.786 MAX. ABS. INTENSITY / VOLUME**2: 58.01557784 RIR: 4.990 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.11 92.21 4.6445 0 0 1 2 32.48 33.52 2.7569 1 0 0 6 37.95 88.16 2.3707 0 1 1 6 37.95 11.84 2.3707 1 0 1 6 38.78 3.96 2.3222 0 0 2 2 51.45 28.86 1.7761 0 1 2 6 51.45 20.62 1.7761 1 0 2 6 57.94 23.97 1.5917 1 1 0 6 59.73 2.22 1.5482 0 0 3 2 61.59 20.35 1.5057 1 1 1 12 68.01 4.21 1.3785 2 0 0 6 69.65 11.63 1.3499 1 0 3 6 69.65 3.99 1.3499 0 1 3 6 71.38 2.33 1.3215 0 2 1 6 71.38 9.77 1.3215 2 0 1 6 71.92 4.61 1.3129 1 1 2 12 81.14 4.47 1.1854 0 2 2 6 81.14 6.05 1.1854 2 0 2 6 83.20 1.97 1.1611 0 0 4 2 88.00 4.37 1.1098 1 1 3 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.