Spinel Menegazzo G, Carbonin S Physics and Chemistry of Minerals 25 (1998) 541-547 Oxidation mechanisms in Al-Mg-Fe spinels. A second stage: alpha-Fe2O3 exsolution Sample: TS11B4, quenched from T = 1150 C after 27 hours _database_code_amcsd 0008154 CELL PARAMETERS: 8.1070 8.1070 8.1070 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 532.820 Density (g/cm3): 3.742 MAX. ABS. INTENSITY / VOLUME**2: 23.58764799 RIR: 2.052 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.96 15.80 4.6806 1 1 1 8 31.21 36.18 2.8663 2 2 0 12 36.77 100.00 2.4444 3 1 1 24 44.71 41.10 2.0268 4 0 0 6 55.53 10.59 1.6548 4 2 2 24 59.22 3.89 1.5602 3 3 3 8 59.22 35.74 1.5602 5 1 1 24 65.09 60.31 1.4331 4 4 0 12 68.47 1.39 1.3703 5 3 1 48 73.94 3.48 1.2818 6 2 0 24 77.15 9.06 1.2363 5 3 3 24 82.42 4.43 1.1701 4 4 4 8 85.55 1.26 1.1352 5 5 1 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.