Spinel
      Pavese A, Artioli G, Russo U, Hoser A
      Physics and Chemistry of Minerals 26 (1999) 242-250
      Cation partitioning versus temperature in (Mg0.70Fe0.23)Al1.97O4
      synthetic spinel by in situ neutron powder diffraction
      Sample: T = 1423 K
      Locality: synthetic
      _database_code_amcsd 0008215

      CELL PARAMETERS:    8.1612   8.1612   8.1612   90.000   90.000   90.000
      SPACE GROUP: Fd3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    543.578
      Density (g/cm3):      3.592
      MAX. ABS. INTENSITY / VOLUME**2:      19.96348077    
      RIR:      1.810
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                18.83          6.25        4.7119    1   1   1         8
                30.99         44.92        2.8854    2   2   0        12
                36.52        100.00        2.4607    3   1   1        24
                38.20          1.73        2.3559    2   2   2         8
                44.40         34.41        2.0403    4   0   0         6
                55.13         11.22        1.6659    4   2   2        24
                58.79         30.62        1.5706    5   1   1        24
                58.79          3.44        1.5706    3   3   3         8
                64.60         50.57        1.4427    4   4   0        12
                73.37          3.16        1.2904    6   2   0        24
                76.55          6.78        1.2446    5   3   3        24
                81.76          2.87        1.1780    4   4   4         8
                89.96          3.60        1.0906    6   4   2        48
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs