Spinel
      Pavese A, Artioli G, Russo U, Hoser A
      Physics and Chemistry of Minerals 26 (1999) 242-250
      Cation partitioning versus temperature in (Mg0.70Fe0.23)Al1.97O4
      synthetic spinel by in situ neutron powder diffraction
      Sample: T = 1573 K
      Locality: synthetic
      _database_code_amcsd 0008216

      CELL PARAMETERS:    8.1768   8.1768   8.1768   90.000   90.000   90.000
      SPACE GROUP: Fd3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    546.701
      Density (g/cm3):      3.572
      MAX. ABS. INTENSITY / VOLUME**2:      19.60591166    
      RIR:      1.787
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                18.80          6.46        4.7209    1   1   1         8
                30.93         44.92        2.8909    2   2   0        12
                36.44        100.00        2.4654    3   1   1        24
                38.13          1.58        2.3604    2   2   2         8
                44.31         34.20        2.0442    4   0   0         6
                55.02         10.92        1.6691    4   2   2        24
                58.67          3.39        1.5736    3   3   3         8
                58.67         30.14        1.5736    5   1   1        24
                64.46         49.11        1.4455    4   4   0        12
                73.21          3.00        1.2929    6   2   0        24
                76.38          6.57        1.2470    5   3   3        24
                81.57          2.78        1.1802    4   4   4         8
                89.75          3.32        1.0927    6   4   2        48
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.