Franklinite Levy D, Pavese A, Hanfland M Physics and Chemistry of Minerals 27 (2000) 638-644 Phase transition of synthetic zinc ferrite spinel (ZnFe2O4) at high pressure, from synchrotron X-ray powder diffraction Sample: P = 0.0 GPa _database_code_amcsd 0008475 CELL PARAMETERS: 8.4412 8.4412 8.4412 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 601.468 Density (g/cm3): 5.324 MAX. ABS. INTENSITY / VOLUME**2: 103.0489763 RIR: 6.302 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.20 4.72 4.8735 1 1 1 8 29.94 36.05 2.9844 2 2 0 12 35.26 100.00 2.5451 3 1 1 24 36.89 7.60 2.4368 2 2 2 8 42.85 13.37 2.1103 4 0 0 6 53.16 12.03 1.7231 4 2 2 24 56.66 28.13 1.6245 5 1 1 24 56.66 5.56 1.6245 3 3 3 8 62.21 38.47 1.4922 4 4 0 12 70.57 4.27 1.3347 6 2 0 24 73.58 8.79 1.2873 5 3 3 24 74.57 3.70 1.2726 6 2 2 24 78.51 1.46 1.2184 4 4 4 8 86.23 5.08 1.1280 6 4 2 48 89.10 5.77 1.0990 5 5 3 24 89.10 7.73 1.0990 7 3 1 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.