Magnetite Yamanaka T, Shimazu H, Ota K Physics and Chemistry of Minerals 28 (2001) 110-118 Electric conductivity of Fe2SiO4-Fe3O4 spinel solid solutions Sample: Fe(3-x)SixO4, x = 0.000, synthesized at 1200 C, 6 GPa Locality: synthetic _database_code_amcsd 0008502 CELL PARAMETERS: 8.3940 8.3940 8.3940 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 591.435 Density (g/cm3): 5.200 MAX. ABS. INTENSITY / VOLUME**2: 90.58268585 RIR: 5.672 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.31 8.15 4.8463 1 1 1 8 30.11 28.19 2.9677 2 2 0 12 35.47 100.00 2.5309 3 1 1 24 37.10 8.40 2.4231 2 2 2 8 43.11 19.99 2.0985 4 0 0 6 53.48 9.26 1.7134 4 2 2 24 57.01 24.22 1.6154 5 1 1 24 57.01 6.19 1.6154 3 3 3 8 62.60 40.01 1.4839 4 4 0 12 71.02 3.29 1.3272 6 2 0 24 74.06 8.30 1.2801 5 3 3 24 75.06 3.86 1.2654 6 2 2 24 79.03 2.49 1.2116 4 4 4 8 86.83 3.52 1.1217 6 4 2 48 89.73 5.05 1.0928 5 5 3 24 89.73 8.13 1.0928 7 3 1 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.