Magnetite Yamanaka T, Shimazu H, Ota K Physics and Chemistry of Minerals 28 (2001) 110-118 Electric conductivity of Fe2SiO4-Fe3O4 spinel solid solutions Sample: Fe(3-x)SixO4, x = 0.288, synthesized at 1200 C, 10 GPa Locality: synthetic _database_code_amcsd 0008504 CELL PARAMETERS: 8.3740 8.3740 8.3740 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 587.217 Density (g/cm3): 5.066 MAX. ABS. INTENSITY / VOLUME**2: 82.32840103 RIR: 5.292 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.35 11.02 4.8347 1 1 1 8 30.19 24.17 2.9607 2 2 0 12 35.56 100.00 2.5249 3 1 1 24 37.19 8.78 2.4174 2 2 2 8 43.21 24.41 2.0935 4 0 0 6 47.32 1.78 1.9211 3 3 1 24 53.62 8.05 1.7093 4 2 2 24 57.16 22.50 1.6116 5 1 1 24 57.16 6.71 1.6116 3 3 3 8 62.77 41.47 1.4803 4 4 0 12 66.00 1.39 1.4155 5 3 1 48 71.22 2.93 1.3240 6 2 0 24 74.27 8.34 1.2770 5 3 3 24 75.28 4.04 1.2624 6 2 2 24 79.26 3.08 1.2087 4 4 4 8 87.09 3.09 1.1190 6 4 2 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.