Gahnite
      Levy D, Pavese A, Sani A, Pischedda V
      Physics and Chemistry of Minerals 28 (2001) 612-618
      Structure and compressibility of synthetic ZnAl2O4 (gahnite) under
      high-pressure conditions, from synchrotron X-ray powder diffraction
      Sample: P = 4.6 GPa
      _database_code_amcsd 0008609

      CELL PARAMETERS:    8.0334   8.0334   8.0334   90.000   90.000   90.000
      SPACE GROUP: Fd3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    518.440
      Density (g/cm3):      4.698
      MAX. ABS. INTENSITY / VOLUME**2:      57.27307462    
      RIR:      3.970
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                19.14          4.45        4.6381    1   1   1         8
                31.50         78.84        2.8402    2   2   0        12
                37.12        100.00        2.4222    3   1   1        24
                45.15          3.68        2.0083    4   0   0         6
                49.45          9.83        1.8430    3   3   1        24
                56.09         23.62        1.6398    4   2   2        24
                59.82          4.17        1.5460    3   3   3         8
                59.82         35.04        1.5460    5   1   1        24
                65.76         40.41        1.4201    4   4   0        12
                69.18          1.22        1.3579    5   3   1        48
                74.74          7.87        1.2702    6   2   0        24
                77.99          9.48        1.2251    5   3   3        24
                86.52          1.20        1.1249    7   1   1        24
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.