Megawite Zhao J, Ross N L, Angel R J Physics and Chemistry of Minerals 31 (2004) 299-305 Tilting and distortion of CaSnO3 perovskite to 7 GPa determined from single-crystal X-ray diffraction Note: P = 0.738 GPa Locality: synthetic _database_code_amcsd 0018606 CELL PARAMETERS: 5.5043 5.6558 7.8687 90.000 90.000 90.000 SPACE GROUP: Pbnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 244.962 Density (g/cm3): 5.606 MAX. ABS. INTENSITY / VOLUME**2: 121.7320476 RIR: 7.070 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 22.54 47.59 3.9446 1 1 0 4 22.60 22.38 3.9344 0 0 2 2 25.26 1.57 3.5263 1 1 1 8 31.64 25.10 2.8279 0 2 0 2 32.13 100.00 2.7856 1 1 2 8 32.53 22.75 2.7522 2 0 0 2 38.00 1.51 2.3678 1 0 3 4 38.12 1.64 2.3607 2 1 1 8 39.23 3.56 2.2963 0 2 2 4 39.98 3.80 2.2552 2 0 2 4 41.34 1.32 2.1841 1 1 3 8 46.02 26.58 1.9723 2 2 0 4 46.14 14.35 1.9672 0 0 4 2 47.53 1.06 1.9131 2 2 1 8 51.22 7.88 1.7836 1 3 0 4 51.86 11.66 1.7632 2 2 2 8 51.94 10.11 1.7604 1 1 4 8 52.43 4.21 1.7452 3 1 0 4 52.62 1.91 1.7394 1 3 1 8 56.66 17.39 1.6244 1 3 2 8 57.03 10.90 1.6149 0 2 4 4 57.59 10.44 1.6004 2 0 4 4 57.79 22.97 1.5953 3 1 2 8 66.08 2.98 1.4139 0 4 0 2 67.21 12.83 1.3928 2 2 4 8 68.14 2.86 1.3761 4 0 0 2 70.81 2.56 1.3306 0 4 2 4 71.39 4.94 1.3213 1 3 4 8 71.79 1.36 1.3149 3 3 0 4 72.39 2.85 1.3055 3 1 4 8 72.81 1.98 1.2989 4 0 2 4 75.61 2.88 1.2577 2 4 0 4 76.37 6.07 1.2471 3 3 2 8 76.56 7.47 1.2445 1 1 6 8 77.08 3.09 1.2374 4 2 0 4 80.11 3.18 1.1980 2 4 2 8 80.78 1.14 1.1897 0 2 6 4 81.26 1.12 1.1839 2 0 6 4 81.56 2.71 1.1804 4 2 2 8 84.36 2.61 1.1481 0 4 4 4 86.27 2.74 1.1276 4 0 4 4 88.18 1.67 1.1080 1 5 0 4 89.69 2.03 1.0932 3 3 4 8 89.81 1.62 1.0921 2 2 6 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.