Ca.3Sr.7TiOGeO4 Ellemann-Olesen R, Malcherek T Physics and Chemistry of Minerals 32 (2005) 531-545 The structure of SrTiOGeO4 and its solid solution with CaTiOGeO4 Note: titanite-type structure Sample: Sr70 _database_code_amcsd 0008992 CELL PARAMETERS: 7.1916 9.0134 6.7387 90.000 113.593 90.000 SPACE GROUP: P2_1/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 400.296 Density (g/cm3): 4.542 MAX. ABS. INTENSITY / VOLUME**2: 28.98933888 RIR: 2.078 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.16 2.64 4.8861 -1 1 1 4 19.70 7.69 4.5067 0 2 0 2 25.38 4.05 3.5088 1 1 1 4 26.94 90.28 3.3097 -2 1 1 4 27.06 26.82 3.2952 2 0 0 2 28.92 95.33 3.0877 0 0 2 2 30.75 27.42 2.9073 -2 0 2 2 32.36 2.02 2.7669 -2 1 2 4 33.16 100.00 2.7017 0 3 1 4 33.26 1.21 2.6938 -1 2 2 4 33.69 53.61 2.6600 2 2 0 4 35.23 8.87 2.5472 0 2 2 4 36.79 13.29 2.4431 -2 2 2 4 37.06 8.92 2.4256 2 1 1 4 38.15 13.69 2.3590 1 3 1 4 38.92 2.12 2.3141 -3 1 1 4 39.25 26.94 2.2956 -2 3 1 4 41.62 2.35 2.1702 -1 1 3 4 42.04 1.55 2.1493 1 2 2 4 42.39 2.35 2.1322 1 4 0 4 42.64 17.03 2.1205 -2 1 3 4 44.70 1.35 2.0272 -3 2 2 4 47.08 13.26 1.9301 2 3 1 4 47.75 10.08 1.9047 2 0 2 2 48.97 6.29 1.8600 2 4 0 4 50.91 1.30 1.7937 -1 3 3 4 51.30 6.66 1.7810 -2 4 2 4 51.36 17.26 1.7792 -4 0 2 2 51.79 11.69 1.7654 -2 3 3 4 52.13 18.43 1.7544 2 2 2 4 52.91 1.48 1.7305 0 5 1 4 54.00 31.45 1.6981 0 3 3 4 54.63 2.15 1.6800 -2 0 4 2 55.53 1.26 1.6549 -4 2 2 4 55.80 8.02 1.6476 4 0 0 2 57.29 16.34 1.6081 -2 5 1 4 58.64 9.25 1.5742 -2 2 4 4 58.69 1.55 1.5730 3 4 0 4 59.91 7.97 1.5439 0 0 4 2 60.47 20.46 1.5309 -4 3 1 4 60.64 1.11 1.5271 1 3 3 4 61.75 4.58 1.5022 0 6 0 2 62.93 4.73 1.4770 2 1 3 4 63.46 9.16 1.4659 2 5 1 4 64.01 1.47 1.4546 2 4 2 4 64.06 11.49 1.4537 -4 0 4 2 64.50 10.22 1.4447 -4 3 3 4 67.39 9.99 1.3897 -2 5 3 4 68.41 1.78 1.3714 -1 6 2 4 68.66 2.19 1.3669 2 6 0 4 69.29 2.21 1.3562 0 5 3 4 69.60 8.49 1.3508 0 6 2 4 69.83 1.66 1.3469 -2 4 4 4 70.24 1.73 1.3400 2 3 3 4 70.57 1.06 1.3346 -2 6 2 4 70.70 1.58 1.3324 -2 1 5 4 72.19 9.63 1.3085 4 3 1 4 75.01 1.92 1.2663 -4 5 1 4 75.50 4.47 1.2593 4 0 2 2 75.96 1.36 1.2527 -3 6 2 4 77.68 2.08 1.2293 -2 3 5 4 78.18 2.23 1.2226 2 0 4 2 80.17 1.37 1.1972 -6 0 2 2 81.59 2.40 1.1800 2 2 4 4 81.63 1.19 1.1795 2 6 2 4 83.18 4.28 1.1614 -4 3 5 4 83.56 1.63 1.1571 -6 -2 2 4 83.73 1.09 1.1552 -6 1 1 4 84.03 2.19 1.1518 2 5 3 4 84.39 3.51 1.1478 -4 6 2 4 84.89 5.45 1.1423 0 3 5 4 85.89 1.26 1.1316 4 5 1 4 86.35 1.14 1.1267 0 8 0 2 87.01 1.12 1.1198 -2 6 4 4 87.97 3.46 1.1101 4 6 0 4 89.15 1.56 1.0984 6 0 0 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.