Ca.5Sr.5TiOGeO4 Ellemann-Olesen R, Malcherek T Physics and Chemistry of Minerals 32 (2005) 531-545 The structure of SrTiOGeO4 and its solid solution with CaTiOGeO4 Note: titanite-type structure Sample: Sr50 _database_code_amcsd 0008994 CELL PARAMETERS: 7.1779 8.9752 6.7105 90.000 113.658 90.000 SPACE GROUP: P2_1/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 395.978 Density (g/cm3): 4.427 MAX. ABS. INTENSITY / VOLUME**2: 26.21841268 RIR: 1.929 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.22 6.62 4.8704 -1 1 1 4 19.78 5.80 4.4876 0 2 0 2 24.01 2.42 3.7065 1 2 0 4 25.49 7.47 3.4948 1 1 1 4 27.00 91.06 3.3023 -2 1 1 4 27.13 23.23 3.2873 2 0 0 2 28.93 1.16 3.0868 2 1 0 4 29.06 100.00 3.0733 0 0 2 2 30.84 26.45 2.8992 -2 0 2 2 32.14 1.22 2.7848 -2 2 1 4 32.45 3.87 2.7588 -2 1 2 4 33.31 97.01 2.6900 0 3 1 4 33.40 4.54 2.6827 -1 2 2 4 33.80 56.32 2.6519 2 2 0 4 35.40 7.87 2.5356 0 2 2 4 36.91 12.26 2.4352 -2 2 2 4 37.20 8.78 2.4173 2 1 1 4 38.31 14.11 2.3493 1 3 1 4 39.00 1.84 2.3093 -3 1 1 4 39.38 23.89 2.2881 -2 3 1 4 41.81 1.54 2.1607 -1 1 3 4 42.57 1.53 2.1235 1 4 0 4 42.80 18.79 2.1128 -2 1 3 4 44.82 2.50 2.0220 -3 2 2 4 47.27 11.49 1.9229 2 3 1 4 47.95 9.50 1.8971 2 0 2 2 49.16 8.04 1.8532 2 4 0 4 51.14 1.16 1.7860 -1 3 3 4 51.46 15.93 1.7757 -4 0 2 2 51.50 8.10 1.7744 -2 4 2 4 52.00 11.18 1.7586 -2 3 3 4 52.36 19.39 1.7474 2 2 2 4 53.16 1.25 1.7231 0 5 1 4 54.26 31.66 1.6904 0 3 3 4 54.87 2.34 1.6733 -2 0 4 2 55.67 1.23 1.6511 -4 2 2 4 55.93 1.60 1.6439 -4 0 3 2 55.94 8.02 1.6437 4 0 0 2 57.53 17.94 1.6020 -2 5 1 4 58.91 8.39 1.5678 -2 2 4 4 58.91 2.25 1.5678 3 4 0 4 60.22 7.51 1.5366 0 0 4 2 60.64 1.18 1.5270 -4 3 2 4 60.65 20.23 1.5269 -4 3 1 4 60.94 1.28 1.5203 1 3 3 4 62.04 4.52 1.4959 0 6 0 2 63.23 4.85 1.4707 2 1 3 4 63.74 9.86 1.4601 2 5 1 4 64.26 11.39 1.4496 -4 0 4 2 64.30 2.06 1.4487 2 4 2 4 64.70 9.41 1.4407 -4 3 3 4 67.69 9.90 1.3842 -2 5 3 4 68.74 1.55 1.3656 -1 6 2 4 68.97 1.92 1.3615 2 6 0 4 69.64 2.21 1.3502 0 5 3 4 69.94 8.38 1.3450 0 6 2 4 70.16 2.09 1.3414 -2 4 4 4 70.58 1.24 1.3344 2 3 3 4 70.89 1.01 1.3294 -1 4 4 4 71.05 1.35 1.3268 -2 1 5 4 72.46 9.60 1.3043 4 3 1 4 75.28 1.90 1.2624 -4 5 1 4 75.80 4.59 1.2550 4 0 2 2 76.28 1.23 1.2482 -3 6 2 4 78.07 1.99 1.2241 -2 3 5 4 78.59 2.26 1.2172 2 0 4 2 80.36 1.47 1.1949 -6 0 2 2 82.02 2.40 1.1748 2 2 4 4 83.52 3.81 1.1575 -4 3 5 4 83.77 1.51 1.1547 -6 -2 2 4 84.47 2.37 1.1469 2 5 3 4 84.73 3.65 1.1440 -4 6 2 4 84.93 1.38 1.1418 2 7 1 4 85.37 5.51 1.1371 0 3 5 4 86.26 1.10 1.1277 4 5 1 4 86.81 1.12 1.1219 0 8 0 2 88.35 3.21 1.1063 4 6 0 4 89.42 1.45 1.0958 6 0 0 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.