Ca.6Sr.4TiOGeO4 Ellemann-Olesen R, Malcherek T Physics and Chemistry of Minerals 32 (2005) 531-545 The structure of SrTiOGeO4 and its solid solution with CaTiOGeO4 Note: titanite-type structure Sample: Sr40 _database_code_amcsd 0008995 CELL PARAMETERS: 7.1757 8.9564 6.6988 90.000 113.708 90.000 SPACE GROUP: P2_1/a X-RAY WAVELENGTH: 1.541838 Cell Volume: 394.188 Density (g/cm3): 4.378 MAX. ABS. INTENSITY / VOLUME**2: 24.88569631 RIR: 1.851 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.24 8.17 4.8645 -1 1 1 4 19.83 5.23 4.4782 0 2 0 2 24.05 3.31 3.7004 1 2 0 4 25.53 10.30 3.4885 1 1 1 4 27.02 93.67 3.3005 -2 1 1 4 27.14 21.61 3.2851 2 0 0 2 29.12 100.00 3.0667 0 0 2 2 30.87 25.84 2.8968 -2 0 2 2 32.49 4.36 2.7562 -2 1 2 4 33.38 95.77 2.6844 0 3 1 4 33.46 4.53 2.6779 -1 2 2 4 33.84 55.09 2.6488 2 2 0 4 35.48 7.76 2.5303 0 2 2 4 36.96 10.79 2.4323 -2 2 2 4 37.25 8.43 2.4139 2 1 1 4 38.39 15.20 2.3447 1 3 1 4 39.02 1.37 2.3083 -3 1 1 4 39.44 22.45 2.2850 -2 3 1 4 40.28 1.55 2.2391 0 4 0 2 41.89 1.47 2.1566 -1 1 3 4 42.66 1.40 2.1194 1 4 0 4 42.86 17.93 2.1099 -2 1 3 4 44.86 2.76 2.0205 -3 2 2 4 45.51 1.14 1.9932 0 1 3 4 47.35 11.75 1.9197 2 3 1 4 48.04 8.61 1.8938 2 0 2 2 49.25 8.01 1.8502 2 4 0 4 51.25 1.05 1.7825 -1 3 3 4 51.48 16.74 1.7751 -4 0 2 2 51.59 7.27 1.7716 -2 4 2 4 52.09 9.93 1.7558 -2 3 3 4 52.46 19.89 1.7443 2 2 2 4 53.28 1.12 1.7195 0 5 1 4 54.39 31.86 1.6869 0 3 3 4 54.97 2.15 1.6705 -2 0 4 2 55.70 1.22 1.6502 -4 2 2 4 55.97 1.36 1.6430 -4 0 3 2 55.98 7.61 1.6425 4 0 0 2 57.64 18.27 1.5993 -2 5 1 4 59.00 2.23 1.5656 3 4 0 4 59.02 8.54 1.5652 -2 2 4 4 60.37 6.90 1.5334 0 0 4 2 60.70 1.01 1.5258 -4 3 2 4 60.70 19.53 1.5257 -4 3 1 4 61.08 1.51 1.5171 1 3 3 4 62.19 4.19 1.4927 0 6 0 2 63.36 4.48 1.4679 2 1 3 4 63.87 9.13 1.4574 2 5 1 4 64.32 11.30 1.4484 -4 0 4 2 64.44 1.69 1.4460 2 4 2 4 64.76 8.63 1.4394 -4 3 3 4 67.83 9.92 1.3817 -2 5 3 4 68.89 1.83 1.3629 -1 6 2 4 69.12 1.44 1.3590 2 6 0 4 69.81 1.89 1.3473 0 5 3 4 70.11 7.51 1.3422 0 6 2 4 70.31 1.85 1.3389 -2 4 4 4 70.74 1.02 1.3318 2 3 3 4 71.05 1.05 1.3267 -1 4 4 4 71.20 1.00 1.3244 -2 1 5 4 72.57 9.07 1.3027 4 3 1 4 75.39 1.41 1.2608 -4 5 1 4 75.92 4.18 1.2533 4 0 2 2 76.43 1.51 1.2462 -3 6 2 4 78.24 1.91 1.2218 -2 3 5 4 78.78 2.21 1.2148 2 0 4 2 79.36 1.02 1.2074 -3 3 5 4 80.39 1.15 1.1945 -6 0 2 2 82.22 2.13 1.1724 2 2 4 4 83.65 3.45 1.1560 -4 3 5 4 83.82 1.47 1.1542 -6 -2 2 4 84.68 2.17 1.1446 2 5 3 4 84.87 3.07 1.1425 -4 6 2 4 85.14 1.23 1.1396 2 7 1 4 85.60 4.89 1.1346 0 3 5 4 86.42 1.08 1.1260 4 5 1 4 88.51 3.09 1.1047 4 6 0 4 89.50 1.27 1.0950 6 0 0 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.