Phase A Holl C M, Smyth J R, Manghnani M H, Amulele G M, Sekar M, Frost D J, Prakapenka V B, Shen G Physics and Chemistry of Minerals 33 (2006) 192-199 Crystal structure and compression of an iron-bearing Phase A to 33 GPa _database_code_amcsd 0009025 CELL PARAMETERS: 7.8678 7.8678 9.5771 90.000 90.000 120.000 SPACE GROUP: P6_3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 513.418 Density (g/cm3): 2.832 MAX. ABS. INTENSITY / VOLUME**2: 9.585928025 RIR: 1.102 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.99 14.30 6.8137 1 0 0 6 15.96 14.29 5.5520 1 0 1 6 22.60 16.54 3.9339 1 1 0 6 22.70 11.24 3.9178 1 0 2 6 24.46 43.52 3.6389 1 1 1 6 26.16 2.05 3.4069 2 0 0 6 27.79 15.70 3.2098 2 0 1 6 29.38 1.34 3.0397 1 1 2 6 30.93 14.08 2.8908 1 0 3 6 32.25 62.33 2.7760 2 0 2 6 34.84 2.71 2.5753 2 1 0 6 36.12 12.05 2.4870 2 1 1 6 36.24 20.50 2.4789 1 1 3 6 37.57 8.08 2.3943 0 0 4 1 39.68 4.40 2.2712 3 0 0 6 39.74 67.20 2.2681 1 2 2 6 39.74 32.80 2.2681 2 1 2 6 39.91 1.81 2.2589 1 0 4 6 44.29 4.57 2.0452 1 1 4 6 45.24 37.04 2.0044 1 2 3 6 45.24 8.20 2.0044 2 1 3 6 46.35 2.25 1.9589 2 0 4 6 47.17 2.80 1.9267 2 2 1 6 49.14 1.64 1.8540 1 3 1 6 49.14 2.57 1.8540 3 1 1 6 49.24 2.72 1.8507 3 0 3 6 52.02 5.52 1.7578 1 3 2 6 52.02 1.06 1.7578 3 1 2 6 52.16 13.91 1.7535 1 2 4 6 52.16 1.50 1.7535 2 1 4 6 53.19 1.45 1.7221 1 1 5 6 53.82 2.58 1.7034 4 0 0 6 54.73 2.53 1.6771 4 0 1 6 54.82 1.43 1.6746 2 2 3 6 55.00 1.25 1.6696 2 0 5 6 55.79 5.14 1.6478 3 0 4 6 56.60 1.19 1.6262 1 3 3 6 56.60 3.26 1.6262 3 1 3 6 57.42 3.19 1.6049 4 0 2 6 59.10 1.31 1.5632 2 3 0 6 59.48 2.86 1.5541 1 0 6 6 59.96 5.10 1.5428 2 3 1 6 60.21 36.63 1.5369 1 2 5 6 60.21 1.25 1.5369 2 1 5 6 61.72 3.83 1.5029 4 0 3 6 62.46 2.32 1.4869 1 4 0 6 62.46 44.48 1.4869 4 1 0 6 62.50 11.37 1.4860 2 3 2 6 62.62 1.41 1.4834 1 3 4 6 64.47 3.16 1.4454 2 0 6 6 66.61 1.07 1.4039 2 3 3 6 67.48 1.15 1.3880 4 0 4 6 68.90 1.10 1.3627 5 0 0 6 69.25 8.91 1.3567 1 2 6 6 69.25 4.25 1.3567 2 1 6 6 69.77 1.57 1.3478 1 4 3 6 70.16 2.22 1.3414 1 0 7 6 72.80 2.28 1.2992 3 3 1 6 73.25 2.80 1.2922 1 1 7 6 75.23 1.14 1.2631 1 4 4 6 75.23 3.60 1.2631 4 1 4 6 75.92 1.50 1.2533 5 0 3 6 76.63 1.07 1.2435 4 2 2 6 76.63 3.48 1.2435 2 4 2 6 78.43 1.59 1.2194 3 1 6 6 78.92 1.80 1.2130 3 3 3 6 80.18 3.12 1.1971 0 0 8 1 80.42 2.52 1.1942 2 4 3 6 81.11 2.28 1.1857 1 5 2 6 81.11 1.31 1.1857 5 1 2 6 82.89 3.10 1.1647 4 0 6 6 85.65 1.57 1.1341 2 4 4 6 87.30 3.67 1.1168 2 3 6 6 88.16 1.56 1.1082 3 1 7 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.